PHYSICAL AGING OF NYLON-66

被引：26
|
作者：
SPINU, I
MCKENNA, GB
机构：
[1] Polymers Division, National Institute of Standards and Technology, Gaithersburg, Maryland
来源：
POLYMER ENGINEERING AND SCIENCE | 1994年 / 34卷 / 24期
关键词：
D O I：
10.1002/pen.760342405
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
The physical aging behavior of nylon 66 as a function of aging temperature, magnitude of applied stress, and aging time has been investigated. Creep tests were performed for samples quenched from a stabilization temperature of 160 degrees C to aging temperatures between 41 degrees C and 65 degrees C, for aging times ranging from 0.5 to 64 h, and at stresses levels from 4 MPa to 24 MPa. Volume recovery was investigated for samples quenched from 160 degrees C to aging temperatures of 41 degrees C and 65 degrees C. The creep compliance curves at different aging times were able to be superimposed. The double logarithmic shift rate was calculated and its dependence on aging temperature and applied stress was determined. Also, it was found that the volume recovery rate depends on the aging temperature. The time-temperature and stress-temperature superpositions were not possible for our data.
引用
收藏
页码：1808 / 1814
页数：7
相关论文
共 50 条
  • [21] KINETICS OF WET OXIDATION OF NYLON-66
    SUNDSTROM, DW
    LUCIANO, AJ
    KLEI, HE
    JOURNAL OF APPLIED POLYMER SCIENCE, 1976, 20 (01) : 207 - 216
  • [22] MALDI investigation of the photooxidation of nylon-66
    Carroccio, S
    Puglisi, C
    Montaudo, G
    MACROMOLECULES, 2004, 37 (16) : 6037 - 6049
  • [23] COPOLYMERS OF NYLON-266 AND NYLON-66 - SYNTHESIS AND CHARACTERIZATION
    GONSALVES, KE
    CHEN, XM
    JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 1993, 31 (03) : 701 - 705
  • [24] PROCESSING INDUCED COPOLYMERIZATION OF NYLON-6 AND NYLON-66
    KHANNA, YP
    TURI, EA
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1984, 188 (AUG): : 23 - POLY
  • [25] BENDING AND TORSIONAL FATIGUE OF NYLON-66 MONOFILAMENTS
    TONEY, M
    SCHWARTZ, P
    JOURNAL OF APPLIED POLYMER SCIENCE, 1992, 46 (11) : 2023 - 2032
  • [26] VISCOELASTICITY AND STABILITY OF NYLON-66 LANGMUIR FILMS
    WANG, LF
    KUO, JF
    CHEN, CY
    EUROPEAN POLYMER JOURNAL, 1995, 31 (08) : 769 - 773
  • [27] THE EFFECT OF STERILIZING RADIATION ON THE PROPERTIES OF NYLON-66
    BIRKINSHAW, C
    BUGGY, M
    DALY, S
    MATERIALS CHEMISTRY AND PHYSICS, 1987, 17 (03) : 239 - 248
  • [28] OBSERVATIONS ON COMPATIBILITY OF NYLON-66 POLYETHYLENE MIXTURES
    OROFINO, TA
    MCNEELY, RL
    JOURNAL OF MACROMOLECULAR SCIENCE-PHYSICS, 1988, B27 (01): : 31 - 39
  • [29] STRESS MASS-SPECTROMETRY OF NYLON-66
    GRAYSON, MA
    LEVY, RL
    WOLF, CJ
    FANTER, DL
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1976, 172 (SEP3): : 137 - 137
  • [30] COPOLYMERS OF NYLON-266 AND NYLON-66 - SYNTHESIS AND CHARACTERIZATION
    CHEN, X
    GONSALVES, KE
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1991, 202 : 12 - POLY
12345