PHYSICAL AGING OF NYLON-66

被引：26
|
作者：
SPINU, I
MCKENNA, GB
机构：
[1] Polymers Division, National Institute of Standards and Technology, Gaithersburg, Maryland
来源：
POLYMER ENGINEERING AND SCIENCE | 1994年 / 34卷 / 24期
关键词：
D O I：
10.1002/pen.760342405
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
The physical aging behavior of nylon 66 as a function of aging temperature, magnitude of applied stress, and aging time has been investigated. Creep tests were performed for samples quenched from a stabilization temperature of 160 degrees C to aging temperatures between 41 degrees C and 65 degrees C, for aging times ranging from 0.5 to 64 h, and at stresses levels from 4 MPa to 24 MPa. Volume recovery was investigated for samples quenched from 160 degrees C to aging temperatures of 41 degrees C and 65 degrees C. The creep compliance curves at different aging times were able to be superimposed. The double logarithmic shift rate was calculated and its dependence on aging temperature and applied stress was determined. Also, it was found that the volume recovery rate depends on the aging temperature. The time-temperature and stress-temperature superpositions were not possible for our data.
引用
收藏
页码：1808 / 1814
页数：7
相关论文
共 50 条
  • [1] POLYMORPHISM IN NYLON-66
    COLCLOUGH, ML
    BAKER, R
    JOURNAL OF MATERIALS SCIENCE, 1978, 13 (12) : 2531 - 2540
  • [2] NYLON-66 AND ALL THAT
    不详
    CHEMISTRY & INDUSTRY, 1952, (16) : 341 - 341
  • [3] FTIR and Thermal Studies on Nylon-66 and 30% Glass Fibre Reinforced Nylon-66
    Charles, Julie
    Ramkumaar, G. R.
    Azhagiri, S.
    Gunasekaran, S.
    E-JOURNAL OF CHEMISTRY, 2009, 6 (01) : 23 - 33
  • [4] HISTORY AND DEVELOPMENT OF NYLON-66
    KOHAN, MI
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1986, 191 : 38 - HIST
  • [5] SEGMENTAL DYNAMICS IN NYLON-66
    MIURA, H
    ENGLISH, AD
    MACROMOLECULES, 1988, 21 (05) : 1543 - 1544
  • [6] ACID HYDROLYSIS OF NYLON-66
    BERKOWITZ, WF
    JOURNAL OF CHEMICAL EDUCATION, 1970, 47 (07) : 536 - +
  • [7] CHAIN DYNAMICS IN NYLON-66
    ENGLISH, AD
    MIURA, H
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1988, 195 : 242 - POLY
  • [8] NYLON-6 AND NYLON-66 - HOW DIFFERENT ARE THEY
    MOORE, RAF
    TEXTILE CHEMIST AND COLORIST, 1989, 21 (02): : 19 - 22
  • [9] MORPHOLOGY OF AXIALLY COMPRESSED NYLON-66
    ANDERSON, FR
    JOURNAL OF APPLIED PHYSICS, 1960, 31 (10) : 1831 - 1831
  • [10] A COLOUR TEST FOR NYLON-66 AND FOR TERYLENE
    ROFF, WJ
    ANALYST, 1954, 79 (938) : 306 - 307
12345