GRAIN-SIZE DEPENDENCE OF COERCIVITY AND PERMEABILITY IN NANOCRYSTALLINE FERROMAGNETS

被引：2195
|
作者：
HERZER, G
机构：
[1] Vacuumschmelze GmbH, D-6450 Hanau, Fed. Rep.
来源：
IEEE TRANSACTIONS ON MAGNETICS | 1990年 / 26卷 / 05期
关键词：
D O I：
10.1109/20.104389
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
Amorphous ribbons of composition Pe74. 5-xCuxNb3Si13. 5B9 (x=0, l at%) have been annealed between about 500°C and 900°C. This produced a series of crystallized samples with grain sizes between about 10nm and 300nm and with coercivities Hcand initial permeabilities μivarying over several orders of magnitude. The best soft magnetic properties (Hc=0.01A/cm and μi=80xl03) were observed for the smallest grain sizes of about 10nm. With increasing grain size D coercivity steeply increases following a D6-power law (up to D=50nm). Hc then runs through a maximum of Hc=30A/cm and decreases again for grain sizes above 150nm according to the well-known l/D-law for poly-crystalline magnets. The initial permeability was found to vary in a similar manner, essentially being inversely proportional to coercivity. The variation of the soft magnetic properties with the average grain size is discussed and compared with the predictions of the random anisotropy model and other theories for the magnetization reversal. © 1990 IEEE
引用
收藏
页码：1397 / 1402
页数：6
相关论文
共 50 条
  • [21] GRAIN-SIZE DEPENDENCE OF THE WEAR OF ALUMINA
    DAVIDGE, RW
    RILEY, FL
    WEAR, 1995, 186 (01) : 45 - 49
  • [22] ON THE GRAIN-SIZE DEPENDENCE OF SECONDARY CREEP
    JONES, SJ
    CHEW, HAM
    JOURNAL OF GLACIOLOGY, 1981, 27 (97) : 517 - 518
  • [23] GRAIN-SIZE DEPENDENCE OF TRM - REVIEW
    DAY, R
    TRANSACTIONS-AMERICAN GEOPHYSICAL UNION, 1976, 57 (12): : 904 - 904
  • [24] Grain-size dependence of millimeters to nanometers
    Conrad, H
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (09): : 2681 - 2695
  • [25] GRAIN-SIZE DEPENDENCE OF WEAR IN CERAMICS
    WU, CC
    RICE, RW
    PLATT, B
    JOHNSON, D
    BEYER, S
    AMERICAN CERAMIC SOCIETY BULLETIN, 1984, 63 (12): : 1474 - 1474
  • [26] A phase field study of frequency dependence and grain-size effects in nanocrystalline ferroelectric polycrystals
    Su, Yu
    Liu, Ning
    Weng, George J.
    ACTA MATERIALIA, 2015, 87 : 293 - 308
  • [27] THE STUDY OF GRAIN-SIZE DEPENDENCE OF YIELD STRESS OF COPPER FOR A WIDE GRAIN-SIZE RANGE
    GERTSMAN, VY
    HOFFMANN, M
    GLEITER, H
    BIRRINGER, R
    ACTA METALLURGICA ET MATERIALIA, 1994, 42 (10): : 3539 - 3544
  • [28] Grain-size dependence of remanence and coercive field of isotropic nanocrystalline composite permanent magnets
    Fischer, R
    Schrefl, T
    Kronmuller, H
    Fidler, J
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1996, 153 (1-2) : 35 - 49
  • [29] Grain size dependence of remanence enhancement and coercivity in nanocrystalline Nd-Fe-B-powders
    Neu, V
    Schultz, L
    Bauer, HD
    NANOSTRUCTURED MATERIALS, 1999, 12 (5-8): : 769 - 774
  • [30] VARIATION OF THE INTERFACIAL ENERGY WITH GRAIN-SIZE IN NANOCRYSTALLINE MATERIALS
    LU, K
    LUCK, R
    PREDEL, B
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1994, 179 (pt 1): : 536 - 540
12345