MICROSTRUCTURES OF AIR ATOMIZED AL-CR POWDERS AND THE MECHANICAL-PROPERTIES OF THE HOT EXTRUDED POWDERS

被引：0
|
作者：
KOBAYASHI, KF [1 ]
FUJII, K [1 ]
KUSUI, J [1 ]
KUBO, K [1 ]
机构：
[1] TOYO ALUMINUM CO LTD,HINO,SHIGA 34114,JAPAN
来源：
ZEITSCHRIFT FUR METALLKUNDE | 1995年 / 86卷 / 04期
关键词：
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Rapidly solidified Al-Cr alloys have been prepared by a gas atomization process. Microstructures were examined as a function of cooling rate and chromium content. At a cooling rate of about 10(4) K/s, solute chromium dissolved in the aluminum matrix up to about 3 at.%. The formation of icosahedral quasi-crystals during solidification prevented the further extension of the solid solubility. Hot extruded Al-2, 3 and 4 at.% Cr specimens from these powders showed 260 to 360 MPa in ultimate tensile strength at room temperature. It increased with increasing chromium content.
引用
收藏
页码：289 / 292
页数：4
相关论文
共 50 条
  • [1] MECHANICAL-PROPERTIES OF HOT-EXTRUDED PRODUCTS FROM CENTRIFUGALLY ATOMIZED POWDERS OF AL-LI AND AL-LI-FE ALLOYS
    HINOJOSATORRES, J
    RIOSJARA, D
    CHAMPIER, G
    MATERIALS TRANSACTIONS JIM, 1990, 31 (08): : 710 - 714
  • [2] THE MICROSTRUCTURE AND PROPERTIES OF WATER ATOMIZED AND EXTRUDED CU-CR ALLOY POWDERS
    CORREIA, JB
    DAVIES, HA
    SELLARS, CM
    SAINZ, J
    GUTIERREZ, I
    CASTRO, F
    FUENTES, M
    SHOHOJI, N
    CARVALHINHOS, H
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 133 : 265 - 269
  • [3] CONSOLIDATION AND MECHANICAL-PROPERTIES OF ATOMIZED MG-BASED AMORPHOUS POWDERS
    KATO, A
    SUGANUMA, T
    HORIKIRI, H
    KAWAMURA, Y
    INOUE, A
    MASUMOTO, T
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1994, 179 : 112 - 117
  • [4] HOT EXTRUSION AND MECHANICAL-PROPERTIES OF RAPIDLY SOLIDIFIED AL AND CU ALLOY POWDERS
    LIU, J
    BACKMARK, U
    ARNBERG, L
    BACKSTROM, N
    GRINDER, O
    SAVAGE, S
    MATERIALS SCIENCE AND ENGINEERING, 1988, 98 : 419 - 423
  • [5] MICROSTRUCTURES AND MECHANICAL-PROPERTIES OF TIAL FABRICATED FROM INTERMETALLIC POWDERS
    NAKAMURA, M
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (13): : 1631 - 1631
  • [6] AMORPHIZATION OF AL-CR ATOMIZED POWDER BY MECHANICAL GRINDING
    KOBAYASHI, KF
    KAWAGUCHI, H
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1994, 181 : 1253 - 1257
  • [7] AMORPHOUS AL-CR ALLOYS BY MECHANICAL GRINDING OF RAPIDLY SOLIDIFIED CRYSTALLINE POWDERS
    KOBAYASHI, KF
    TACHIBANA, N
    SHINGU, PH
    JOURNAL OF MATERIALS SCIENCE, 1990, 25 (2A) : 801 - 804
  • [8] Distribution of heterogeneous nucleants in Al-Cr alloy powders
    Adkins, N.J.E., 1600, (A133):
  • [9] Microstructure and Mechanical Properties of Al-Ni-Mm-(Cu, Fe) Alloys Hot-Extruded from Gas-Atomized Powders
    Kim, Hye-Sung
    KOREAN JOURNAL OF MATERIALS RESEARCH, 2006, 16 (02): : 137 - 143
  • [10] THE DISTRIBUTION OF HETEROGENEOUS NUCLEANTS IN AL-CR ALLOY POWDERS
    ADKINS, NJE
    TSAKIROPOULOS, P
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 133 : 767 - 770
12345