THE SHEAR-STRENGTH AND THE FAILURE MODE OF PLASMA-SPRAYED HYDROXYAPATITE COATING TO BONE - THE EFFECT OF COATING THICKNESS

被引:131
|
作者
WANG, BC
LEE, TM
CHANG, E
YANG, CY
机构
[1] NATL CHENG KUNG UNIV,DEPT MAT ENGN,TAINAN,TAIWAN
[2] NATL CHENG KUNG UNIV,DEPT ORTHOPAED SURG,TAINAN,TAIWAN
来源
关键词
D O I
10.1002/jbm.820271012
中图分类号
R318 [生物医学工程];
学科分类号
0831 ;
摘要
Plasma-sprayed hydroxyapatite coated (HAC) 50 and 200 mum thick on Ti-6Al-4V cylinders was transcortically implanted in the femora of canines to evaluate in detail the effect of coating thickness on the push-out shear strength and failure mode examined under scanning electron microscope after the periods of 4, 6, 8, and 12 weeks. The HAC coating exhibited higher shear strength at 50 mum than at 200 mum. Its failure mode was conclusively at or near the HAC-bone interface, and the slight attack of body fluid had not degraded the implant to the extent that failure occurred at the HAC-Ti alloy interface after 12 weeks of observation. For 200 mum-HAC, failure was found at the HAC-bone interface, inside the HAC lamellar splat layer and at the HAC-Ti alloy substrate interface, depending on the period of implantation. It was also deduced that the variation of failure mode of 200 mum-HAC with time could not be accounted for by the attack of body fluid alone; the degradation must be a synergetic adverse result of residual stress in the HAC and the attack of body fluid. (C) 1993 John Wiley & Sons, Inc.
引用
收藏
页码:1315 / 1327
页数:13
相关论文
共 50 条
  • [1] Effect of coating thickness on the shear strength and failure mode of plasma sprayed hydroxyapatite coatings to bone
    Wang, B.C.
    Lee, T.M.
    Chang, E.
    Yang, C.Y.
    Biomedical Engineering - Applications, Basis and Communications, 1992, 4 (06): : 605 - 609
  • [2] The influence of residual stress on the shear strength between the bone and plasma-sprayed hydroxyapatite coating
    Yang, Yung-Chin
    Yang, Chyun-Yu
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN MEDICINE, 2008, 19 (03) : 1051 - 1060
  • [3] The influence of residual stress on the shear strength between the bone and plasma-sprayed hydroxyapatite coating
    Yung-Chin Yang
    Chyun-Yu Yang
    Journal of Materials Science: Materials in Medicine, 2008, 19 : 1051 - 1060
  • [4] Nanostructure of plasma-sprayed hydroxyapatite coating
    E. I. Suvorova
    V. V. Klechkovskaya
    V. V. Bobrovsky
    Yu. D. Khamchukov
    V. V. Klubovich
    Crystallography Reports, 2003, 48 : 872 - 877
  • [5] Nanostructure of plasma-sprayed hydroxyapatite coating
    Suvorova, EI
    Klechkovskaya, VV
    Bobrovsky, VV
    Khamchukov, YD
    Klubovich, VV
    CRYSTALLOGRAPHY REPORTS, 2003, 48 (05) : 872 - 877
  • [6] Effect of the thickness of plasma-sprayed coating on bond strength and thermal fatigue characteristics
    Choi, HM
    Kang, BS
    Choi, WK
    Choi, DG
    Choi, SK
    Kim, JC
    Park, YK
    Kim, GM
    JOURNAL OF MATERIALS SCIENCE, 1998, 33 (24) : 5895 - 5899
  • [7] Effect of the thickness of plasma-sprayed coating on bond strength and thermal fatigue characteristics
    H. M. Choi
    B. S. Kang
    W. K. Choi
    D. G. Choi
    S. K. Choi
    J. C. Kim
    Y. K. Park
    G. M. Kim
    Journal of Materials Science, 1998, 33 : 5895 - 5899
  • [8] Ultrastructural features of the bone response to a plasma-sprayed hydroxyapatite coating in sheep
    Hemmerle, J
    Oncag, A
    Erturk, S
    JOURNAL OF BIOMEDICAL MATERIALS RESEARCH, 1997, 36 (03): : 418 - 425
  • [9] EFFECT OF HEAT-TREATMENT ON THE MICROSTRUCTURE OF PLASMA-SPRAYED HYDROXYAPATITE COATING
    JI, HX
    MARQUIS, PM
    BIOMATERIALS, 1993, 14 (01) : 64 - 68
  • [10] Failure of the plasma-sprayed coating of lanthanum hexaluminate
    Cao, X. Q.
    Zhang, Y. F.
    Zhang, J. F.
    Zhong, X. H.
    Wang, Y.
    Ma, H. M.
    Xu, Z. H.
    He, L. M.
    Lu, F.
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2008, 28 (10) : 1979 - 1986