ALTERNATING STRESS-CORROSION CRACKING ON STEEL X 20 CR 13 AT PULSATING TENSILE STRESS IN AGENTS CONTAINING CHLORIDE-IONS AT TEMPERATURES UP TO 200 DEGREES CENTIGRADE

被引：7

作者：

SCHMITTTHOMAS, KG ^{[1
]}

TENSI, HM ^{[1
]}

LEIDIG, A ^{[1
]}

SCHMID, R ^{[1
]}

机构：

[1] TECH UNIV MUNICH,INST MET & METALLKUNDE,MUNICH,FED REP GER

来源：

ARCHIV FUR DAS EISENHUTTENWESEN | 1975年 / 46卷 / 03期

关键词：

D O I：

10.1002/srin.197504010

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

引用

页码：223 / 227

页数：5

共 8 条

[1] Fatigue Stress Corrosion Cracking of Steel X20Cr13 Under Pulsating Tensile Stress in Media Containing Chloride Ions at Temperatures up to 200 degree C.
Schmitt-Thomas, Karlheinz G.
Tensi, Hans M.
Leidig, Alfred
Schmid, Robert
Archiv fuer das Eisenhuettenwesen, 1975, 46 (03): : 223 - 227
[2] STRESS-CORROSION CRACKING OF AISI 304 STAINLESS-STEEL IN CHLORIDE CONTAINING AMMONIUM-SULFATE SOLUTIONS AT 220-DEGREES-F
TONG, HS
SWARTZ, DJ
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1979, 126 (03) : C111 - C111
[3] STRESS-CORROSION CRACKING OF 316L AUSTENITIC STAINLESS-STEEL IN BORIC-ACID AND CHLORIDE SOLUTIONS AT 200 DEGREES-C
KASRI, R
DESJARDINS, D
PUIGGALI, M
CLEMENT, C
REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 1993, 90 (02): : 261 - 271
[4] The influence of sulphate ions on stress corrosion cracking for stainless steel AISI 321 with constant extension rate in aqueous chloride solution at temperatures up to 280°C
Barkleit, G
Schneider, F
Mummert, K
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 1997, 48 (12): : 822 - 828
[5] STRESS-CORROSION CRACKING OF SENSITIZED AISI-304 STAINLESS-STEEL IN AQUEOUS CHLORIDE SOLUTIONS CONTAINING SULFUR SPECIES AT 50-C THROUGH 200-C
LEE, JK
SZKLARSKASMIALOWSKA, Z
CORROSION, 1988, 44 (08) : 560 - 565
[6] Stress corrosion cracking of the chromium steel X 210 Cr 12 in chloride and sulphate containing solutions Part II: Influence of media on SCC-behaviour
Jaeger, G
Schneider, F
Mummert, K
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 1998, 49 (06): : 408 - 413
[7] Stress corrosion cracking of the chromium steel X 210 Cr 12 in chloride and sulphate containing solutions - Part 1: Influence of loading conditions on SCC - behaviour
Jaeger, G
Schneider, F
Mummert, K
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 1998, 49 (06): : 397 - 407
[8] STRESS-CORROSION CRACKING OF SENSITIZED AISI-304 STAINLESS-STEEL IN OXYGENATED HIGH-TEMPERATURE CHLORIDE SOLUTIONS CONTAINING CUPRIC (CU-2+) AND LEAD (PB-2+) IONS
MACDONALD, DD
EGHAN, AK
SZKLARSKASMIALOWSKA, Z
CORROSION, 1985, 41 (08) : 474 - 484

← 1 →