POLAR GLASS STRUCTURE FOR 2ND-ORDER NONLINEAR OPTICS PREPARED BY THE LANGMUIR-BLODGETT METHOD USING AMORPHOUS POLYMERS WITH AN AZO-DYE

In order to obtain Langmuir-Blodgett (LB) films for second-order nonlinear optics, LB films of the amorphous copolymers synthesized from methyl methacrylate and 2-(N-ethyl-N-(4-(4-nitrophenyl)azo)phenyl)aminoethyl acrylate were investigated. From the measurement of F-A isotherms and UV and visible spectra of the Langmuir (L) film, it was estimated that the azo-dye moiety was squeezed out from the air-water interface into the subphase, and the dipoles of azo-dye align uniaxially in the direction perpendicular to the interface. The L film could be deposited into X-type multilayers by the horizontal lifting method, resulting in the formation of "polar glass."