Synthesis, characterization and potential biomedical applications of N-succinimidyl ester functionalized, polypyrrole-coated polystyrene latex particles

N-Succinimidyl ester functionalized polypyrrole-coated polystyrene latex particles (PSE-PPyNSE) were prepared by the in situ copolymerization of pyrrole and the active ester-functionalized pyrrole (pyrrole-NSE) in the presence of polystyrene latex particles. Polystyrene microspheres were prepared by emulsion polymerization (PSE) leading to particles having a diameter of 450 nm. These PSE particles were precoated with poly(N-vinylpyrrolidone) prior to the in situ copolymerization of pyrrole and pyrrole-NSE. The initial comonomer concentration fractions were 25/75, 50/50 and 75/25 for pyrrole and pyrrole-NSE, respectively. The PPy-coated PSE particles were characterized in terms of morphology, particle size, electrophoretic mobility and chemical composition. The study of morphology by means of scanning electron microscopy showed roughening of the underlying PSE particles owing to the addition of PPyNSE, the overlayer thickness of which was estimated to be around 7 nm. Moreover, loading PPyNSE overlayers resulted in a shift of the electrophoretic mobility from −5.31 μm cm/V s to a very small but positive value (0.082–0.112 μm cm/V s). X-ray photoelectron spectroscopy and IR spectroscopy permitted the detection of pyrrole-NSE repeat units at the surface indicating that pyrrole and pyrrole-NSE did indeed copolymerize. The PSE-PPyNSE particles were further evaluated as bioadsorbents of human serum albumin used as a test protein. For this study, PSE-PPyNSE50 particles, synthesized from a comonomer feed ratio of 50/50 in pyrrole/pyrrole-NSE, were used and were shown to attach efficiently human serum albumin macromolecules with a maximum amount of 0.2 mg m−2.