Phase composition of the products of nitriding ferrosilicon with zircon concentrate additives

被引：0
|
作者：
L. N. Chukhlomina
O. G. Vitushkina
N. N. Golobokov
V. I. Vereshchagin
机构：
[1] Tomsk Scientific Center of a Siberian Branch of the Russian Academy of Sciences,
[2] Tomsk Polytechnical University,undefined
来源：
Glass and Ceramics | 2008年 / 65卷
关键词：
Silicon Nitride; Ferrosilicon; Zircon Concentrate; Iron Silicon; Iron Silicide;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The process of nitride formation during combustion of iron silicon with the addition of zircon concentrate in nitrogen gas is investigated. It is determined that in the presence of zircon (5–70%) ferrosilicon burns in a surface regime, and the products of combustion are multiphase. For the optimal parameters of synthesis (nitrogen pressure 4–7 MPa and sample diameter 35–40 mm) the products of combustion are a composition consisting of a ceramic constituent (Si3N4-ZrO2-Si2N2O) and iron (α-Fe). The method of acidic enrichment is used to obtain a composite ceramic powder with iron mass content 0.5%
引用
收藏
页码：38 / 40
页数：2
相关论文
共 50 条
  • [1] Phase composition of the products of nitriding ferrosilicon with zircon concentrate additives
    Chukhlomina, L. N.
    Vitushkina, O. G.
    Golobokov, N. N.
    Vereshchagin, V. I.
    GLASS AND CERAMICS, 2008, 65 (1-2) : 38 - 40
  • [2] Phase composition of the products of combustion of ferrosilicon in nitrogen with fluorine-containing additives present
    L. N. Chukhlomina
    O. G. Vitushkina
    V. I. Vereshchagin
    Glass and Ceramics, 2008, 65 : 236 - 239
  • [3] PHASE COMPOSITION OF THE PRODUCTS OF COMBUSTION OF FERROSILICON IN NITROGEN WITH FLUORINE-CONTAINING ADDITIVES PRESENT
    Chukhlomina, L. N.
    Vitushkina, O. G.
    Vereshchagin, V. I.
    GLASS AND CERAMICS, 2008, 65 (7-8) : 236 - 239
  • [4] Phase composition and morphology of products of combustion of ferrosilicon in nitrogen
    Chukhlomina, L. N.
    Maksimov, Yu. M.
    Vitushkina, O. G.
    Golobokov, N. N.
    Vereshchagin, V. I.
    GLASS AND CERAMICS, 2007, 64 (1-2) : 63 - 65
  • [5] Phase composition and morphology of products of combustion of ferrosilicon in nitrogen
    L. N. Chukhlomina
    Yu. M. Maksimov
    O. G. Vitushkina
    N. N. Golobokov
    V. I. Vereshchagin
    Glass and Ceramics, 2007, 64 : 63 - 65
  • [6] Influence of temperature on phase composition of nitridation products from ferrosilicon alloy
    Yang Jingzhou
    Huang Zhaohui
    Xia Yinfeng
    Wang Xinying
    Fang Minghao
    Liu Yan'gai
    RARE METAL MATERIALS AND ENGINEERING, 2007, 36 : 273 - 275
  • [7] Combustion of Ferrosilicon–Zircon Mixtures in Nitrogen Gas: Impact of Aluminum Additives
    O. G. Kryukova
    K. A. Bolgaru
    A. N. Avramchik
    International Journal of Self-Propagating High-Temperature Synthesis, 2021, 30 : 236 - 240
  • [8] Combustion of Ferrosilicon-Zircon Mixtures in Nitrogen Gas: Impact of Aluminum Additives
    Kryukova, O. G.
    Bolgaru, K. A.
    Avramchik, A. N.
    INTERNATIONAL JOURNAL OF SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS, 2021, 30 (04) : 236 - 240
  • [9] Composition and toxicity of petroleum products and their additives
    Henry, JA
    HUMAN & EXPERIMENTAL TOXICOLOGY, 1998, 17 (02): : 111 - 123
  • [10] Effects of Additives on Phase Composition,Microstructure,and Properties of Zirconia Products Fired at Different Temperatures
    TAN Qinghua
    China's Refractories, 2010, 19 (04) : 25 - 29
12345