Primary and Anelastic Creep of a Near α-Ti Alloy and Their Dependencies on Stress and Temperature

被引:2
|
作者
Es-Souni M. [1 ]
机构
[1] Univ. Appl. Sci., Mat. Test. Joining, 24149 Kiel
关键词
Anelastic creep; Primary creep; Ti-alloys;
D O I
10.1023/A:1009879328879
中图分类号
学科分类号
摘要
The primary creep behaviour of a high temperature near α-Ti alloy Ti6242Si has been investigated in the temperature range from 500 to 625° C, and the stress range from 80 to 450 MPa. The results are analysed in terms of the dependencies of stress on strain (strain hardening) and on strain rate (strain rate sensitivity). Furthermore, full unloading experiments were conducted in order to gain additional information as to the nature of primary creep. It is shown that primary creep can be described by an athermal component, strain hardening, with a mean strain hardening coefficient of 0.37, and a thermally activated component, strain rate sensitivity, with a strain rate sensitivity coefficient suggesting a mechanism based on climb controlled recovery. This is confirmed by the activation energy of 259 kJ/mol determined at different stresses, which is similar to the activation energy of Ti self diffusion in α-Ti. The anelastic strain obtained on full unloading was analysed in its fast stage in a similar way. The kinetics of anelastic creep and its activation energy are in many aspects very similar to those of primary creep. It is thought that, in the stress and temperature range investigated, primary creep is to a relatively high extent anelastic in nature, and is controlled by the climb controlled bow out of pinned dislocation segments, particularly dislocations pinned at lath boundaries.
引用
收藏
页码:211 / 228
页数:17
相关论文
共 50 条
  • [1] Primary and anelastic creep in a high temperature near alpha-Ti alloy: Effects of microstructure and stress
    EsSouni, M
    EUROMAT 97 - PROCEEDINGS OF THE 5TH EUROPEAN CONFERENCE ON ADVANCED MATERIALS AND PROCESSES AND APPLICATIONS: MATERIALS, FUNCTIONALITY & DESIGN, VOL 1: METALS AND COMPOSITES, 1997, : 233 - 236
  • [2] Primary, secondary and anelastic creep of a high temperature near α-Ti alloy Ti6242Si
    Es-Souni, M
    MATERIALS CHARACTERIZATION, 2000, 45 (02) : 153 - 164
  • [3] Primary creep and anelastic recovery of a near γ-TiAl intermetallic
    Dudzinski, D
    Beddoes, J
    Zhao, L
    CREEP AND FRACTURE OF ENGINEERING MATERIALS AND STRUCTURES, 1996, : 289 - 298
  • [4] Effect of primary α content on creep and creep crack growth behaviour of near α-Ti alloy
    Omprakash, C. M.
    Satyanarayana, D. V. V.
    Kumar, V.
    MATERIALS SCIENCE AND TECHNOLOGY, 2011, 27 (09) : 1427 - 1432
  • [5] Stress and temperature dependence of creep in Alloy 600 in primary water
    Yi, YS
    Was, GS
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2001, 32 (10): : 2553 - 2560
  • [6] Stress and temperature dependence of creep in Alloy 600 in primary water
    Yongsun Yi
    Gary S. Was
    Metallurgical and Materials Transactions A, 2001, 32 : 2553 - 2560
  • [7] The temperature and stress dependent primary creep of CP-Ti at low and intermediate temperature
    Peng, Jian
    Zhou, Chang-Yu
    Dai, Qiao
    He, Xiao-Hua
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 611 : 123 - 135
  • [8] Primary Creep and Steady-State Creep of Ti65 Alloy
    Yue K.
    Liu J.
    Yang R.
    Wang Q.
    Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2020, 34 (02): : 151 - 160
  • [9] Anelastic spectroscopy in a Ti alloy used as biomaterial
    Almeida, L. H.
    Grandini, C. R.
    Caram, R.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 521-22 : 59 - 62
  • [10] Creep behavior of Ti-600 alloy at elevated temperature
    Zeng, Li-Ying
    Yang, Guan-Jun
    Hong, Quan
    Zhao, Yong-Qing
    Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2011, 32 (02): : 81 - 85