Opto-chemical response of Makrofol-KG to swift heavy ion irradiation

In the present study, the effects of swift heavy ion beam irradiation on the structural, chemical and optical properties of Makrofol solid-state nuclear track detector (SSNTD) were investigated. Makrofol-KG films of 40 μm thickness were irradiated with oxygen beam (O8 + ) with fluences ranging between 1010 ion/cm2 and 1012 ion/cm2. Structural, chemical and optical properties were investigated using X-ray diffraction, FTIR spectroscopy and UV–visible spectroscopy methods. It is observed that the direct and indirect band gaps of Makrofol-KG decrease after the irradiation. The XRD study shows that the crystalline size in the films decreases at higher fluences. The intensity plots of FTIR measurements indicate the degradation of Makrofol at higher fluences. Roughness of the surface increases at higher fluence.