Sensitive Adsorption Stripping Voltammetric Determination of Reserpine by a Glassy Carbon Electrode Modified with Multi-Wall Carbon Nanotubes

Adsorption stripping voltammetry, a very sensitive electroanalytical method, was employed to determine reserpine, a kind of anti-hypertensive drug. In 0.1 M phosphate buffer with a pH of 6.0, reserpine was accumulated at a multi-wall carbon nanotubes (MWNT)-modified glassy carbon electrode (GCE) surface under the condition of open-circuit. In the following anodic sweep from 0.20 to 1.00 V, reserpine, adsorbed at the MWNT-modified GCE surface, was oxidized and yielded a sensitive oxidation peak at 0.64 V. Due to its unique structure and extraordinary properties, MWNT shows a ten times higher accumulation efficiency toward reserpine, compared with a bare GCE. Hence, the amount of reserpine at the MWNT-modified GCE surface increases significantly, and finally the oxidation peak current improves greatly. The experimental conditions, such as supporting electrolyte, pH value, the amount of MWNT-DHP suspension, accumulation time and scan rate, were optimized for the measurement of reserpine, and a sensitive electroanalytical method was proposed for reserpine determination. The oxidation peak current varies linearly with the concentration of reserpine over the range of 2×10−8 to 1×10−5 M, and the detection limit is 7.5×10−9 M after 4 min open-circuit accumulation. The relative standard deviation at 1×10−6 M reserpine was about 4.7% (n=7), indicating excellent reproducibility. This new method was successfully demonstrated with reserpine injections and tablets.