Preparation and characterization of nanocrystalline and mesoporous strontium titanate thin films at room temperature

The low temperature perovskite-type strontium titanate (SrTiO3) thin films and powders with nanocrystalline and mesoporous structure were prepared by a straightforward particulate sol–gel route. The prepared sol had a narrow particle size distribution with hydrodynamic diameter of about 17 nm. X-ray diffraction (XRD) revealed that the synthesized powders had a perovskite-SrTiO3 structure with preferable orientation growth along the (1 0 0) direction. TEM images showed that the average crystallite size of the powders annealed in the range 300–800°C was around 8 nm. FE-SEM analysis and AFM images revealed that the deposited thin films had mesoporous and nanocrystalline structure with the average grain size of 25 nm at 600°C. Based on Brunauer–Emmett–Taylor (BET) analysis, the synthesized powders showed mesoporous structure with BET surface area in the range 92–75 m2/g at 400–600°C. One of the smallest crystallite sizes and one of the highest surface areas reported in the literature were obtained, which can be used in many applications, such as photocatalysts.