Effect of yttria(Y2O3) coating for high temperature oxidation resistance of 9Cr-1Mo steel

被引：0
|
作者：
D. Ghosh
S. Mukherjee
S. Das
S. K. Mitra
机构：
[1] NDT and Metallurgy Group,Metallurgical and Materials Engineering Department
[2] CMERI,undefined
[3] National Institute of Technology,undefined
[4] National Institute of Technology,undefined
来源：
Protection of Metals and Physical Chemistry of Surfaces | 2016年 / 52卷
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
This paper investigates the effect of yttria (Y2O3) coating on high temperature oxidation behaviour of low alloy 9 Cr–1Mo steel. The superficial coating is Y2O3 was prepared for experimental investigation. The isothermal corrosion study of uncoated and coated specimens was carried out in air oxidation environment at 973 K for 8 h. The corrosion rate and reaction kinetics were studied and the post corroded scales were characterized in SEM, EDS and XRD. The results clearly indicate that Y2O3 coated specimen improves the high temperature oxidation resistance than uncoated specimens. The improvement of oxidation resistance in presence of Y2O3 coating can be attributed to the changed mechanism of scale growth from outer cation migration to inner anion migration and enhancement of scale adhesion with the substrate. Further, enhancement of scale adhesion with the substrate in case of Y2O3 coating also improves the oxidation resistance. The detail mechanism of the oxidation of Y2O3 coated and uncoated specimen is further discussed in this paper.
引用
收藏
页码：737 / 743
页数：6
相关论文
共 50 条
  • [1] Effect of yttria(Y2O3) coating for high temperature oxidation resistance of 9Cr-1Mo steel
    Ghosh, D.
    Mukherjee, S.
    Das, S.
    Mitra, S. K.
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2016, 52 (04) : 737 - 743
  • [2] Microstructure studies of an aluminide coating on 9Cr-1Mo steel during high temperature oxidation
    Chang, Yo-Yu
    Tsaur, Charng-Cheng
    Rock, James C.
    SURFACE & COATINGS TECHNOLOGY, 2006, 200 (22-23): : 6588 - 6593
  • [3] The Effect of Cr Addition on the Strength and High Temperature Oxidation Resistance of Y2O3 Dispersion Strengthened Mo Composites
    Guan, Haochen
    Lv, Chongshan
    Ding, Qingming
    Wang, Guangda
    Xiong, Ning
    Zhou, Zhangjian
    MATERIALS, 2024, 17 (11)
  • [4] Study of high-temperature oxidation of modified 9Cr-1Mo steel
    Peña-Ballesteros, Darío Yesid
    Vásquez-Quintero, Custodio
    Ingenieria y Universidad, 2011, 15 (02): : 359 - 372
  • [5] High temperature oxidation behaviour of yttria ( Y2O3) coated low alloy steel
    Ghosh, D.
    Mukherjee, S.
    Das, S.
    SURFACE ENGINEERING, 2014, 30 (07) : 524 - 528
  • [6] THE EFFECT OF TEMPERATURE ON THE EROSION CORROSION OF 9CR-1MO STEEL
    LEVY, A
    MAN, YF
    WEAR, 1986, 111 (02) : 161 - 172
  • [7] Development of sol-gel alumina coating on 9Cr-1Mo ferritic steel and their oxidation behavior at high temperature
    Singh, I. B.
    Modi, O. P.
    Ruhi, G.
    JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2015, 74 (03) : 685 - 691
  • [8] DEVELOPMENT OF NEW 9CR-1MO TYPE STEEL .3. WELDABILITY OF 9CR-1MO TYPE STEEL
    SAKURAI, H
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 73 (05): : S503 - S503
  • [9] Effect of Y2O3 Superficial Coating on the High Temperature Corrosion Behavior of 2.25Cr–1Mo Steel in SO2 + O2 Atmosphere
    D. Ghosh
    S. K. Mitra
    Journal of The Institution of Engineers (India): Series D, 2012, 93 (2) : 59 - 63
  • [10] The effect of microstructure on the oxidation and carburisation of 9Cr-1Mo steel exposed to CO2
    Coghlan, L.
    Yan, S.
    Shin, A.
    Pearson, J.
    Jepson, M. A. E.
    Higginson, R. L.
    CORROSION SCIENCE, 2021, 191
12345