Structure, microstructure, and thermopower of highest manganese silicide crystals grown from zinc solution-melt

被引：0
|
作者：
F. Yu. Solomkin
V. K. Zaitsev
N. F. Kartenko
A. S. Kolosova
A. Yu. Samunin
G. N. Isachenko
机构：
[1] Russian Academy of Sciences,Ioffe Physicotechnical Institute
来源：
Technical Physics | 2008年 / 53卷
关键词：
72.20.Pa;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
MnSi1.71–1.75 single crystals are grown using the combination of solidification from solution-melt and the Bridgman crystal growth technique. The single crystals represent tetrahedral bipyramids and correspond to the highest manganese silicide (HMS) modification with lattice parameters a = b = 5.52(1) Å and c = 65.7(8) Å. The thermopower measured between the parallel faces of these single crystals is anomalously high for plain HMS (180–190 μV/K).
引用
收藏
页码：800 / 801
页数：1
相关论文
共 50 条
  • [1] Structure, microstructure, and thermopower of highest manganese silicide crystals grown from zinc solution-melt
    Solomkin, F. Yu.
    Zaitsev, V. K.
    Kartenko, N. F.
    Kolosova, A. S.
    Samunin, A. Yu.
    Isachenko, G. N.
    TECHNICAL PHYSICS, 2008, 53 (06) : 800 - 801
  • [2] Crystallization of highest manganese silicide MnSi1.71-1.75 from tin-lead solution-melt
    Solomkin, F. Yu.
    Zaitsev, V. K.
    Kartenko, N. F.
    Kolosova, A. S.
    Samunin, A. Yu.
    Isachenko, G. N.
    TECHNICAL PHYSICS, 2008, 53 (12) : 1636 - 1637
  • [3] Crystallization of highest manganese silicide MnSi1.71–1.75 from tin-lead solution-melt
    F. Yu. Solomkin
    V. K. Zaitsev
    N. F. Kartenko
    A. S. Kolosova
    A. Yu. Samunin
    G. N. Isachenko
    Technical Physics, 2008, 53 : 1636 - 1637
  • [4] Crystallization and properties of CrSi2 single crystals grown from a tin solution-melt
    Solomkin, F. Yu.
    Zaitsev, V. K.
    Kartenko, N. F.
    Kolosova, A. S.
    Orekhov, A. S.
    Samunin, A. Yu.
    Isachenko, G. N.
    TECHNICAL PHYSICS, 2010, 55 (01) : 151 - 153
  • [5] Crystallization and properties of CrSi2 single crystals grown from a tin solution-melt
    F. Yu. Solomkin
    V. K. Zaitsev
    N. F. Kartenko
    A. S. Kolosova
    A. S. Orekhov
    A. Yu. Samunin
    G. N. Isachenko
    Technical Physics, 2010, 55 : 151 - 153
  • [6] POLARITY AND PROPERTIES OF CDSNP2 AND CDSNAS2 CRYSTALS GROWN FROM A SOLUTION-MELT
    DANILOV, VI
    DROZDOV, YN
    ZVONKOV, BN
    KARPOVICH, IA
    PORTNOV, VN
    IZVESTIYA VYSSHIKH UCHEBNYKH ZAVEDENII FIZIKA, 1981, (11): : 49 - 52
  • [7] Plate structure of high-temperature superconductor crystals of Bi grown in cavities of charge material solution-melt in KCl
    Martovitskij, V.P.
    Rodin, V.V.
    Kratkie Soobshcheniya po Fizike, 2003, (07): : 13 - 22
  • [8] MICROSTRUCTURE OF LARGE CRYSTALS GROWN FROM THE MELT
    SOKOLOV, VA
    SINEV, AN
    GUSEV, IB
    NIKOLAEV, VI
    SOVIET JOURNAL OF OPTICAL TECHNOLOGY, 1984, 51 (09): : 530 - 532
  • [9] IMPROVED BI-(2201) SINGLE-CRYSTALS GROWN IN CAVITIES FORMED IN KCL SOLUTION-MELT
    MARTOVITSKY, VP
    GORINA, JI
    KALJUSHNAIA, GA
    SOLID STATE COMMUNICATIONS, 1995, 96 (11) : 893 - 896
  • [10] STRUCTURE OF ZINC SULFIDE SINGLE CRYSTALS GROWN FROM MELT UNDER PRESSURE
    ANANEVA, GV
    DUBENSKI.KK
    RYSKIN, AI
    KHILKO, GI
    SOVIET PHYSICS SOLID STATE,USSR, 1968, 10 (06): : 1417 - &
12345