High-temperature corrosion-resistance performance of electro-thermal explosion spraying coating

被引：0
|
作者：
Shi-cheng Wei
Bin-shi Xu
Hai-dou Wang
Guo Jin
机构：
[1] National Key Laboratory for Remanufacturing,
来源：
Journal of Central South University of Technology | 2005年 / 12卷
关键词：
high temperature corrosion-resistance; electro-thermal explosion spraying; coating; TG174.442;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
As a new spraying technology used in the remanufacturing engineering, electro-thermal explosion spraying holds a lot of advantages. Electro-thermal explosion spraying coating aliquation phenomena are reduced and non-crystal, micro-crystal and millimicron-crystal and other microstructure are formed. The corrosion-resistance ability of electro-thermal explosion spraying coating in high temperature environment was surveyed respectively. SEM equipped with EDS was employe to analyzed the microstructure of spraying coating before and after corrosion. The corrosion-resistance mechanism of the spraying coating was discussed.
引用
收藏
页码：195 / 198
页数：3
相关论文
共 50 条
  • [1] High-temperature corrosion-resistance performance of electro-thermal explosion spraying coating
    魏世丞
    徐滨士
    王海斗
    金国
    Journal of Central South University, 2005, (S2) : 195 - 198
  • [2] High-temperature corrosion-resistance performance of electro-thermal explosion spraying coating
    Wei, SC
    Xu, BS
    Wang, HD
    Jin, G
    JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2005, 12 (2): : 195 - 198
  • [3] High-temperature corrosion-resistance performance of electro-thermal explosion plasma spraying FeAl-base coatings
    Wei, Shi-cheng
    Xu, Bin-shi
    Wang, Hai-dou
    Jin, Guo
    Lv, Hong
    SURFACE & COATINGS TECHNOLOGY, 2007, 201 (15): : 6768 - 6771
  • [4] Comparison on corrosion-resistance performance of electro-thermal explosion plasma spraying FeAl-based coatings
    Wei, Shi-Cheng
    Xu, Bin-Shi
    Wang, Hai-Dou
    Jin, Guo
    Lv, Hong
    SURFACE & COATINGS TECHNOLOGY, 2007, 201 (9-11): : 5294 - 5297
  • [5] Anticorrosion performance of electro-thermal explosion spraying coatings at high temperature
    National Key Laboratory for Remanufacturing Technology, Academy of Armored Forces Engineering, Beijing 100072, China
    Jinshu Rechuli, 2006, 1 (53-56):
  • [6] HIGH-TEMPERATURE CORROSION-RESISTANCE
    BIRKS, N
    MEIER, GH
    PETTIT, FS
    JOURNAL OF METALS, 1987, 39 (12): : 28 - 31
  • [7] Characteristics of Molybdenum Coating Prepared by Electro-thermal Explosion Spraying with Constraining Tube
    Zhu Liang
    Qiao Hetao
    Zhang Pengfei
    Bi Xuesong
    Zhao Jinfeng
    RARE METAL MATERIALS AND ENGINEERING, 2013, 42 (07) : 1488 - 1491
  • [8] ELECTRODEPOSITS FOR HIGH-TEMPERATURE CORROSION-RESISTANCE
    HONEY, FJ
    WRIDE, V
    KEDWARD, EC
    PLATING AND SURFACE FINISHING, 1986, 73 (10): : 42 - 46
  • [9] Microstructure and wear resistance of electro-thermal explosion sprayed stellite coating used for remanufacturing
    金国
    徐滨士
    王海斗
    李庆芬
    魏世丞
    Journal of Central South University, 2005, (S2) : 207 - 210
  • [10] Microstructure and wear resistance of electro-thermal explosion sprayed stellite coating used for remanufacturing
    Jin, G
    Xu, BS
    Wang, HD
    Li, QF
    Wei, SC
    JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2005, 12 (2): : 207 - 210
12345