Properties of oriented strandboard made of wood species from Brazilian planted forests: Part 1: 80 mm-long strands of Pinus taeda L.Eigenschaften von OSBs aus verschiedenen Hölzern brasilianischer Wälder hergestellt

This research is part of a general study on the properties of oriented strandboard (OSB) using wood strands of species from Brazilian planted forests. The OSB industry is the latest wood related activity established in Brazil. In this particular part of the study, 80 mm long strands of Pinus taeda L. were bonded using two resin types (urea-formaldehyde and phenol-formaldehyde) at two levels of resin content (5% and 8%) to produce three-layer cross-aligned OSB to a face to core layer ratio of 1:2 and target density of 0.75 g/cm3. Physical and mechanical properties of the boards were evaluated according to ASTM standard D 1037-96a (1997) and the results compared to standards available as requirements for commercial structural panels. The results indicate that all the mechanical properties evaluated were above the requirements set forth by the Canadian standard CSA O437.0 (1993) for structural panels. The results of Janka hardness were in average 4 folds higher than the minimal requirements for Grade R-1 waferboard. Screw withdrawal values were also above the minimum required by grade M-3 of ANSI A208.1 standard (1993). Nevertheless, values of thickness swelling and water absorption were very high. The low dimensional stability may be related to the high density of the boards (“springback” effect) and also to the fact that no wax was used.