Effects of Dy2BaCuO5 contents on microstructure and mechanical strength of Ag-added Dy-Ba-Cu-O bulk superconductors

被引：29
|
作者：
Nariki, S
Sakai, N
Murakami, M
Hirabayashi, I
机构：
[1] ISTEC, Supercond Res Lab, Koto Ku, Tokyo 1350062, Japan
[2] Shibaura Inst Technol, Minato Ku, Tokyo 1088548, Japan
来源：
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS | 2004年 / 412卷
关键词：
melt-textured bulk; mechanical strength; microstructure; DyBaCu3Oy; Dy2BaCuO5;
D O I：
10.1016/j.physc.2004.01.084
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
We investigated the microstructure and mechanical strength of Ag-added DyBa2Cu3Oy (Dy123) bulk superconductors with various Dy2BaCuO5 (Dy211) contents. Single-grain Dy123 bulk samples 32 min in diameter with the addition of 5-40 mol% of Dy211 and 10 wt.% of Ag2O were fabricated in air. The sample with 5 mol% Dy211 contained many macro-cracks in the ab-plane. The amount of cracks decreased with increasing Dy211 content. Three-point bending tests were performed at room temperature to measure the mechanical properties. The average bending strength of the sample with 5 mol% Dy211 was 73 MPa. The strength was improved to 95 MPa with an addition of 40 mol% Dy211. (C) 2004 Elsevier B.V. All rights reserved.
引用
收藏
页码：651 / 656
页数：6
相关论文
共 31 条
  • [1] Effect of Dy2BaCuO5 addition on trapped magnetic fields in Dy-Ba-Cu-O bulk superconductors
    Nariki, S
    Sakai, N
    Murakami, M
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2002, 66 (04) : 315 - 319
  • [2] Superconducting properties of Dy-Ba-Cu-O bulk superconductors
    Nariki, S
    Murakami, M
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2002, 15 (05): : 786 - 790
  • [3] Flux creep properties in Dy-Ba-Cu-O bulk superconductors
    Enomoto, H
    Inoue, K
    Nariki, S
    Murakami, M
    Takizawa, T
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2002, 378 : 513 - 516
  • [4] Microstructure and superconducting properties of Dy-Ba-Cu-O bulk superconductors fabricated in different oxygen atmospheres
    Tanaka, H
    Nariki, S
    Sakai, N
    Hirabayashi, I
    Murakami, M
    Takizawa, T
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2005, 426 : 660 - 665
  • [5] Peak effect in field trapping properties of large grain Dy-Ba-Cu-O/Ag bulk superconductors
    Nariki, S
    Murakami, M
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2002, 378 : 759 - 763
  • [6] Effects of Zn doping on the superconducting properties of the melt textured Dy-Ba-Cu-O bulk superconductors
    Latha, B
    Ikuta, H
    Mizutani, U
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS BRIEF COMMUNICATIONS & REVIEW PAPERS, 2004, 43 (03): : 970 - 975
  • [7] Interaction between ring permanent magnets and bulk Dy-Ba-Cu-O superconductors
    Kurabayashi, H.
    Horikoshi, S.
    Suzuki, A.
    Ikeda, M.
    Wongsatanawarid, A.
    Seki, H.
    Akiyama, S.
    Hiragushi, M.
    Murakami, M.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2010, 470 (20): : 1853 - 1855
  • [8] SIMULATED GROWTH AND MICROSTRUCTURE OF DYBA2CU3O7-X WITH AND WITHOUT DY2BACUO5 ADDITION
    VANDEWALLE, N
    CLOOTS, R
    AUSLOOS, M
    JOURNAL OF MATERIALS RESEARCH, 1995, 10 (02) : 268 - 273
  • [9] Enhancement of critical currents and trapped fields of melt textured ZnO doped Dy-Ba-Cu-O bulk superconductors
    Latha, B
    Ikuta, H
    Mizutani, U
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2004, 412 : 566 - 570
  • [10] Temperature dependence of the mechanical properties of melt-processed Dy-Ba-Cu-O bulk superconductors evaluated by three point bending tests
    Katagiri, K.
    Nyilas, A.
    Sato, T.
    Hatakeyama, Y.
    Hokari, T.
    Teshima, H.
    Iwamoto, A.
    Mito, T.
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2006, 19 (07): : S545 - S549
1234