The microstructural change of C-S-H at elevated temperature in Portland cement/GGBFS blended system

被引：74
|
作者：
Jia, Zijian [1 ]
Chen, Chun [1 ]
Shi, Jinjie [1 ]
Zhang, Yamei [1 ]
Sun, Zhengming [1 ]
Zhang, Peigen [1 ]
机构：
[1] Southeast Univ, Jiangsu Key Lab Construct Mat, Sch Mat Sci & Engn, Nanjing, Jiangsu, Peoples R China
来源：
CEMENT AND CONCRETE RESEARCH | 2019年 / 123卷
基金：
中国国家自然科学基金;
关键词：
High temperature; Portland cement; GGBFS; Microstructure; C-S; -H; CALCIUM-SILICATE-HYDRATE; PASTE; MODEL; STRENGTH; CONCRETE; BEHAVIOR; EXPOSURE; GEL; OPC;
D O I：
10.1016/j.cemconres.2019.05.018
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
This investigation focuses on the change of C-S-H gels in Portland cement (PC) paste and PC/ground granulated blast-furnace slag (GGBFS) blended paste at elevated temperature up to 800 degrees C. Spark-like phase, which might be spurrite, can be found in the inner product of C3S in PC paste when the temperature is higher than 600 degrees C. The gels in PC paste show an obvious change in composition in comparison with the gels in GGBFS blended paste at elevated temperature. After 600 degrees C, the continuous decomposition and shrinkage of C-S-H gels results in the increase of small pores (10-40 nm) in both pastes. The nitrogen adsorption results show that some gels, which should be C-A-S-H in GGBFS blended paste, are quite stable at high temperature. The results of this study provide a comprehensive understanding of the different behavior between gels in PC paste and GGBFS blended paste at high temperature.
引用
收藏
页数：10
相关论文
共 50 条
  • [1] THE COMPOSITION OF THE C-S-H PHASES IN PORTLAND-CEMENT PASTES
    RAYMENT, DL
    MAJUMDAR, AJ
    CEMENT AND CONCRETE RESEARCH, 1982, 12 (06) : 753 - 764
  • [2] Hydration of Portland cement accelerated by C-S-H seeds at different temperatures
    Pedrosa, Herman Camilo
    Reales, Oscar Mendoza
    Reis, Victoria Dias
    Paiva, Maria das Dores
    Rego Fairbairn, Eduardo Moraes
    CEMENT AND CONCRETE RESEARCH, 2020, 129
  • [3] Impact of C-S-H seeding on hydration and strength of slag blended cement
    Li, Xuerun
    Bizzozero, Julien
    Hesse, Christoph
    CEMENT AND CONCRETE RESEARCH, 2022, 161
  • [4] Ettringite and C-S-H Portland cement phases for waste ion immobilization: A review
    Gougar, MLD
    Scheetz, BE
    Roy, DM
    WASTE MANAGEMENT, 1996, 16 (04) : 295 - 303
  • [5] Modelling microstructural changes of ordinary Portland cement paste at elevated temperature
    Zhang, Qi
    Ye, Guang
    ADVANCES IN CEMENT RESEARCH, 2019, 31 (01) : 26 - 42
  • [6] Estimation of C-S-H content in a blended cement paste using water adsorption
    Olson, RA
    Jennings, HM
    CEMENT AND CONCRETE RESEARCH, 2001, 31 (03) : 351 - 356
  • [7] Portland and Belite Cement Hydration Acceleration by C-S-H Seeds with Variable w/c Ratios
    Morales-Cantero, Alejandro
    Cuesta, Ana
    De la Torre, Angeles G.
    Mazanec, Oliver
    Borralleras, Pere
    Weldert, Kai S.
    Gastaldi, Daniela
    Canonico, Fulvio
    Aranda, Miguel A. G.
    MATERIALS, 2022, 15 (10)
  • [8] Effect of Corrosive Solutions on C-S-H Microstructure in Portland Cement Paste with Fly Ash
    丁庆军
    WANG Huan
    HU Chenguang
    张高展
    JournalofWuhanUniversityofTechnology(MaterialsScience), 2016, 31 (05) : 1002 - 1007
  • [9] Effect of corrosive solutions on C-S-H microstructure in portland cement paste with fly ash
    Qingjun Ding
    Huan Wang
    Chenguang Hu
    Gaozhan Zhang
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2016, 31 : 1002 - 1007
  • [10] Variation in the composition of C-S-H gel in portland cement pastes cured at various temperatures
    Department of Engineering Materials, University of Sheffield, Sheffield S1 3JD, United Kingdom
    不详
    J Am Ceram Soc, 11 (3237-3241):
12345