Direct Decomposition of NO on C-type Cubic Rare Earth Oxides Based on Y2O3

被引：21
|
作者：
Tsujimoto, Soichiro [1 ]
Mima, Koji [1 ]
Masui, Toshiyuki [1 ]
Imanaka, Nobuhito [1 ]
机构：
[1] Osaka Univ, Fac Engn, Dept Appl Chem, Suita, Osaka 5650871, Japan
来源：
CHEMISTRY LETTERS | 2010年 / 39卷 / 05期
关键词：
NITRIC-OXIDE; PEROVSKITE OXIDE; SOLID-SOLUTIONS; CATALYSTS; NITROGEN; N-2; OXYGEN; O-2; BA;
D O I：
10.1246/cl.2010.456
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
C-type cubic (Y0.99-xTbxBa0.01)(2)O2.99+delta (0 <= x <= 0.4) catalysts were prepared by coprecipitation. The NO decomposition activities at 1173 K were higher than that of (Gd0.7Y0.26Ba0.04)(2)O-2.96 reported previously. The highest catalytic activity was obtained for (Y0.69Tb0.3Ba0.01)(2)O2.99+delta, and 100% NO conversion into N-2 and O-2 was realized at 1173 K on this catalyst. Furthermore, the conversion ratio was maintained as high as 70.8% even in the presence of 5 vol % oxygen.
引用
收藏
页码：456 / 457
页数：2
相关论文
共 50 条
  • [1] Effects of Tb and Ba introduction on the reaction mechanism of direct NO decomposition over C-type cubic rare earth oxides based on Y2O3
    Tsujimoto, Soichiro
    Yasuda, Keisuke
    Masui, Toshiyuki
    Imanaka, Nobuhito
    CATALYSIS SCIENCE & TECHNOLOGY, 2013, 3 (08) : 1928 - 1936
  • [2] Crystal field strength in C-type cubic rare earth oxides
    Antic-Fidancev, E
    Hölsä, J
    Lastusaari, M
    JOURNAL OF ALLOYS AND COMPOUNDS, 2002, 341 (1-2) : 82 - 86
  • [3] Direct NO decomposition over C-type cubic Y2O3-Pr6O11-Eu2O3 solid solutions
    Masui, Toshiyuki
    Uejima, Shunji
    Tsujimoto, Soichiro
    Nagai, Ryosuke
    Imanaka, Nobuhito
    CATALYSIS TODAY, 2015, 242 : 338 - 342
  • [4] Direct Decomposition of NO into N2 and O2 on C-type Cubic Y2O3-ZrO2 and Y2O3-ZrO2-BaO
    Tsujimoto, Soichiro
    Wang, Xiaojing
    Masui, Toshiyuki
    Imanaka, Nobuhito
    BULLETIN OF THE CHEMICAL SOCIETY OF JAPAN, 2011, 84 (07) : 807 - 811
  • [5] Direct decomposition of nitrogen monoxide over C-type cubic Y2O3-Pr6O11 solid solutions
    Tsujimoto, Soichiro
    Masui, Toshiyuki
    Imanaka, Nobuhito
    RSC ADVANCES, 2014, 4 (03): : 1146 - 1149
  • [6] C-type cubic Y2O3 single crystal growth by electrolysis of Y3+ ion conducting solid electrolyte
    Masui, T
    Kim, YW
    Imanaka, N
    SOLID STATE IONICS, 2004, 174 (1-4) : 67 - 71
  • [7] Direct decomposition of nitric oxide into nitrogen and oxygen over C-type cubic Y2O3-ZrO2 solid solutions
    Masaki, Hiroyuki
    Masui, Toshiyuki
    Imanaka, Nobuhito
    JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 451 (1-2) : 406 - 409
  • [8] Direct Decomposition of N2O over C-Type Cubic Yb2O3-Co3O4 Catalysts
    Cho, Chang-Min
    Nunotani, Naoyoshi
    Imanaka, Nobuhito
    BULLETIN OF THE CHEMICAL SOCIETY OF JAPAN, 2019, 92 (07) : 1148 - 1153
  • [9] Direct N2O decomposition over Yb2O3-CuO catalysts with C-type cubic structure
    Cho, Chang-Min
    Nunotani, Naoyoshi
    Imanaka, Nobuhito
    FUNCTIONAL MATERIALS LETTERS, 2020, 13 (08)
  • [10] Direct decomposition of nitric oxide over C-type cubic (Gd1-x-yYxBay)2O3-y solid solutions
    Imanaka, Nobuhito
    Masui, Toshiyuki
    Masaki, Hiroyuki
    ADVANCED MATERIALS, 2007, 19 (21) : 3660 - +
12345