Tempering embrittlement of 2.25Cr-1Mo steel for, a long term of service

被引：0
|
作者：
Hua, L [1 ]
Xu, H [1 ]
Wang, ZW [1 ]
Wang, ZD [1 ]
机构：
[1] E China Univ Sci & Technol, Shanghai 200237, Peoples R China
来源：
ENVIRONMENT EFFECTS ON FRACTURE AND DAMAGE | 2004年
关键词：
tempering embrittlement; hydrogen induced cracking; impurity segregation; intergranular fracture;
D O I：
暂无
中图分类号：
O414.1 [热力学];
学科分类号：
摘要：
The microstructures and mechanical properties are investigated in this paper for a hydrogenation reactor steel 2.25Cr-1Mo after long-term service. The material exposed at 427 degreesC for 10 years as a testing block in reactor vessel show appreciable temper embrittlement. The fracture toughness K(IC) at room temperature is lower because of tempering situation and hydrogen absorption. Coarse grain and impurity segregation at grain boundary are observed from micrography. The results show that fracture mode changes from quasi-cleavage to intergranular when temper embrittlement becomes more serious. It also shows that the ratio of intergranular fracture-to transgranular fracture will be bigger after cathodical hydrogen charging.
引用
收藏
页码：105 / 109
页数：5
相关论文
共 50 条
  • [1] Mechanism of Embrittlement and De-Embrittlement for 2.25Cr-1Mo Steel
    ZHANG Xi-liang
    JournalofIronandSteelResearch(International), 2011, 18 (03) : 47 - 51
  • [2] Degradation in tensile and creep properties of 2.25Cr-1Mo steel by long term service in plant
    Ohba, T
    Kimura, K
    Abe, F
    Yagi, K
    Nonaka, I
    MATERIALS SCIENCE AND TECHNOLOGY, 2005, 21 (04) : 476 - 482
  • [3] The influence of prior microstructure on tempering stages in 2.25Cr-1Mo steel
    Parameswaran, P
    Vijayalakshmi, M
    Raghunathan, VS
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2002, 21 (05) : 251 - 267
  • [4] HYDROGEN AND TEMPER EMBRITTLEMENT INTERACTIONS IN FATIGUE OF 2.25CR-1MO STEEL
    HIPPSLEY, CA
    MATERIALS SCIENCE AND TECHNOLOGY, 1987, 3 (11) : 912 - 922
  • [5] INFLUENCE OF MICROSTRUCTURE ON HYDROGEN EMBRITTLEMENT BEHAVIOR OF 2.25CR-1MO STEEL
    VALENTINI, R
    SOLINA, A
    MATERIALS SCIENCE AND TECHNOLOGY, 1994, 10 (10) : 908 - 914
  • [6] STUDY ON THE HYDROGEN EFFECT ON THE TEMPER EMBRITTLEMENT OF 2.25Cr-1Mo STEEL
    Zhang Xiliang
    Zhou Changyu
    PROCEEDINGS OF THE 18TH INTERNATIONAL CONFERENCE ON NUCLEAR ENGINEERING 2010, VOL 5, 2011, : 179 - 184
  • [7] OXIDATION BEHAVIOR OF 2.25CR-1MO STEEL WITH PRIOR TEMPERING AT DIFFERENT TEMPERATURES
    RAMAN, RKS
    GNANAMOORTHY, JB
    ROY, SK
    OXIDATION OF METALS, 1993, 40 (1-2): : 21 - 36
  • [8] Evolution of Carbide Precipitates in 2.25Cr-1Mo Steel during Long-Term Service in a Power Plant
    Yang, Yong
    Chen, Yiren
    Sridharan, Kumar
    Allen, Todd R.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2010, 41A (06): : 1441 - 1447
  • [9] Effect of oxidation on the long-term creep behavior of a 2.25Cr-1Mo steel
    Endo, T
    Shi, JZ
    Yosiizu, H
    Monma, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1997, 83 (11): : 742 - 747
  • [10] Evolution of Carbide Precipitates in 2.25Cr-1Mo Steel during Long-Term Service in a Power Plant
    Yong Yang
    Yiren Chen
    Kumar Sridharan
    Todd R. Allen
    Metallurgical and Materials Transactions A, 2010, 41 : 1441 - 1447
12345