Corrosion-induced concrete cracking model considering corrosion product-filled paste at the concrete/steel interface

被引：80
|
作者：
Zhao, Yuxi [1 ]
Dong, Jianfeng [1 ]
Wu, Yingyao [1 ]
Jin, Weiliang [1 ]
机构：
[1] Zhejiang Univ, Inst Struct Engn, Hangzhou 310058, Zhejiang, Peoples R China
来源：
CONSTRUCTION AND BUILDING MATERIALS | 2016年 / 116卷
基金：
中国国家自然科学基金;
关键词：
Corrosion layer; Corrosion product-filled paste; Cracking model; Steel reinforced concrete; INDUCED COVER CRACKING; REINFORCED-CONCRETE; STEEL CORROSION; RUST LAYER; REBAR CORROSION; PENETRATION; DAMAGE; BARS;
D O I：
10.1016/j.conbuildmat.2016.04.097
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
When steel corrosion happens in concrete, the corrosion products migrate to the pores at the steel/concrete interface. The relationship between the thickness of the corrosion product-filled paste (CP) and that of the corrosion layer (CL) was analysed and established. This relationship can describe the phenomenon that the corrosion products are filling in the concrete pores and accumulating at the steel/concrete interface simultaneously. Based on this relationship, a corrosion-induced concrete surface cracking model which can quantitatively consider corrosion product-filled paste at the concrete/steel interface is proposed. This model is verified and in reasonable agreement with the experimental results. The possibility of the application of the proposed corrosion-induced cracking model to the non-uniform corrosion case is also discussed. (c) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：273 / 280
页数：8
相关论文
共 50 条
  • [1] Influence of environment on the development of corrosion product-filled paste and a corrosion layer at the steel/concrete interface
    Zhao, Yuxi
    Zhang, Xiaowen
    Jin, Weiliang
    CORROSION SCIENCE, 2017, 124 : 1 - 9
  • [2] Monitoring corrosion-induced concrete cracking adjacent to the steel-concrete interface
    Alhede, Andreas
    Dijkstra, Jelke
    Lundgren, Karin
    MATERIALS AND STRUCTURES, 2023, 56 (09)
  • [3] Monitoring corrosion-induced concrete cracking adjacent to the steel-concrete interface
    Andreas Alhede
    Jelke Dijkstra
    Karin Lundgren
    Materials and Structures, 2023, 56
  • [4] Corrosion-Induced Cracking Model of Concrete Considering a Transverse Constraint
    Yan, Xinrong
    Tian, Ye
    Yan, Dongming
    Pan, Litan
    Zhou, Qiujing
    Zhang, Guoyi
    Pei, Liang
    Lu, Xiang
    Jiang, Bo
    Pan, Weifeng
    Wang, Daquan
    Chen, Bin
    Li, Yiran
    Luo, Lin
    MATERIALS, 2024, 17 (13)
  • [5] Steel corrosion and corrosion-induced cracking in recycled aggregate concrete
    Zhao, Yuxi
    Dong, Jianfeng
    Wu, Yingyao
    Wang, Hailong
    Li, Xiangmin
    Xu, Qingfeng
    CORROSION SCIENCE, 2014, 85 : 241 - 250
  • [6] Analytical model of corrosion-induced cracking of concrete considering the stiffness of reinforcement
    Bhargava, K
    Ghosh, AK
    Mori, Y
    Ramanujam, S
    STRUCTURAL ENGINEERING AND MECHANICS, 2003, 16 (06) : 749 - 769
  • [7] Steel rebar corrosion and corrosion-induced cracking in reinforced foamed concrete
    Luo, Yongheng
    Zhu, Qilin
    Chen, Depeng
    Liu, Chunlin
    Pan, Suiwei
    FRONTIERS IN MATERIALS, 2022, 9
  • [8] Impact of Defects in Steel-Concrete Interface on the Corrosion-Induced Cracking Propagation of the Reinforced Concrete
    Wenjun Zhu
    Chengyue Yang
    Zhongxu Yu
    Junhua Xiao
    Yude Xu
    KSCE Journal of Civil Engineering, 2023, 27 : 2621 - 2628
  • [9] Impact of Defects in Steel-Concrete Interface on the Corrosion-Induced Cracking Propagation of the Reinforced Concrete
    Zhu, Wenjun
    Yang, Chengyue
    Yu, Zhongxu
    Xiao, Junhua
    Xu, Yude
    KSCE JOURNAL OF CIVIL ENGINEERING, 2023, 27 (06) : 2621 - 2628
  • [10] Development of the corrosion-filled paste and corrosion layer at the steel/concrete interface
    Zhao, Yuxi
    Ding, Hangjie
    Jin, Weiliang
    CORROSION SCIENCE, 2014, 87 : 199 - 210
12345