Enhanced magnetocaloric properties of La0.8K0.2-xPbxMnO3 nanoparticles by optimizing Pb doping concentrations

Polycrystalline La(0.8)K(0.2-x)Pb(x)MnO3 (x = 0.05, 0.10, 0.15, 0.20) ceramics were successfully prepared by flash combustion route and their structural, morphological, magnetic and magnetocaloric properties were investi-gated. Structural analyses using X-ray diffraction reveal that all samples are crystallized in the rhombohedral structure and belong to R <(3) over bar > c space group. The increase of Pb doping does not modify the crystalline structure but changes the grain size and lattice parameters. X-ray photoelectron spectroscopy (XPS) fitting results of Mn 2p peaks confirmed the coexistence of Mn3+ and Mn4+ ions which contribute to the double exchange interactions improving the ferromagnetic order in the samples. The magnetization's temperature and magnetic field de-pendences indicate a second-order ferromagnetic-paramagnetic transition of the ceramics. A significant mag-netic entropy change near room temperature was observed for La0.8K0.1Pb0.1MnO3, showing considerable magnetocaloric properties. Furthermore, electron paramagnetic resonance spectroscopy (EPR) was also used to examine the ferromagnetic-paramagnetic transition.