Formation Mechanism of CaS-Al2O3 Inclusions in Low Sulfur Al-Killed Steel After Calcium Treatment

被引：48
|
作者：
Xu, Jianfei [1 ]
Huang, Fuxiang [1 ]
Wang, Xinhua [1 ]
机构：
[1] Univ Sci & Technol Beijing, Sch Met & Ecol Engn, 30 Xueyuan Rd, Beijing 100083, Peoples R China
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE | 2016年 / 47卷 / 02期
关键词：
SHAPED NONMETALLIC INCLUSIONS; EVOLUTION; SYSTEM; PLATES;
D O I：
10.1007/s11663-016-0599-8
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The laboratory experiments of alumina inclusions modified by calcium treatment in Al-killed steel were carried out at 1873 K (1600 degrees C), and the inclusions in steel samples were characterized at 1, 5, and 10 minutes after calcium addition. The results show that the type of inclusions after calcium treatment was determined by the sulfur and T.O contents of steel. CaS-Al2O3 inclusions were obtained in steels with high sulfur and low T.O contents. The mass ratio between CaS and Al2O3 was determined by T.Ca and T.O contents of steel. The influence of holding time after calcium addition on the composition of inclusions was negligible. The thermodynamics for the formation of CaS-Al2O3 inclusions after calcium treatment was discussed, and a simple formation mechanism was proposed. Moreover, the CaO, Al2O3, and CaS contents in the inclusions were predicted through the sulfur, total calcium (T.Ca), and T.O contents, and it was found that the CaO content decreases with increasing S/T.O, while (pctCaS)/(pctAl(2)O(3))(1/3) increases with increasing T.Ca/T.O. (C) The Minerals, Metals & Materials Society and ASM International 2016
引用
收藏
页码：1217 / 1227
页数：11
相关论文
共 50 条
  • [1] Formation Mechanism of CaS-Al2O3 Inclusions in Low Sulfur Al-Killed Steel After Calcium Treatment
    Jianfei Xu
    Fuxiang Huang
    Xinhua Wang
    Metallurgical and Materials Transactions B, 2016, 47 : 1217 - 1227
  • [2] Effectiveness of calcium treatment on nonmetallic inclusions in Al-killed steel
    Bao, Y.-P. (baoyp@ustb.edu.cn), 1600, University of Science and Technology Beijing (35):
  • [3] Formation Mechanism of CaS-Bearing Inclusions and the Rolling Deformation in Al-Killed, Low-Alloy Steel with Ca Treatment
    Guang Xu
    Zhouhua Jiang
    Yang Li
    Metallurgical and Materials Transactions B, 2016, 47 : 2411 - 2420
  • [4] Formation Mechanism of CaS-Bearing Inclusions and the Rolling Deformation in Al-Killed, Low-Alloy Steel with Ca Treatment
    Xu, Guang
    Jiang, Zhouhua
    Li, Yang
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2016, 47 (04): : 2411 - 2420
  • [5] Calcium Transfer to Oxide Inclusions in Al-Killed Steel Without Calcium Treatment
    Deepoo Kumar
    Petrus Christiaan Pistorius
    Metallurgical and Materials Transactions B, 2021, 52 : 163 - 177
  • [6] Calcium Transfer to Oxide Inclusions in Al-Killed Steel Without Calcium Treatment
    Kumar, Deepoo
    Pistorius, Petrus Christiaan
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2021, 52 (01): : 163 - 177
  • [7] Modification of MgO•Al2O3 spinel inclusions in Al-killed steel by Ca-treatment
    Yang, Shu-feng
    Li, Jing-she
    Wang, Zai-fei
    Li, Jiao
    Lin, Lin
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2011, 18 (01) : 18 - 23
  • [8] Novel mechanism for the modification of Al2O3-based inclusions in ultra-low carbon Al-killed steel considering the effects of magnesium and calcium
    Guo, Jing
    Cheng, Shu-sen
    Guo, Han-jie
    Mei, Ya-guang
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2018, 25 (03) : 280 - 287
  • [9] Effect of Calcium Content on Characteristics of Inclusions in an Al-Killed Steel
    Wang, Weijian
    Zhang, Lifeng
    STEEL RESEARCH INTERNATIONAL, 2024, 95 (06)
  • [10] Modification of MgO·Al2O3 spinel inclusions in Al-killed steel by Ca-treatment
    Shu-feng Yang
    Jing-she Li
    Zai-fei Wang
    Jiao Li
    Lin Lin
    International Journal of Minerals, Metallurgy, and Materials, 2011, 18 : 18 - 23
12345