Polarization behaviour and lifetime of IrO2-Ta2O5-SnO2/Ti anodes in p-phenolsulfonic acid solutions for tin plating

被引：44
|
作者：
Morimitsu, M [1 ]
Tamura, H
Matsunaga, M
Otogawa, R
机构：
[1] Kyushu Inst Technol, Dept Appl Chem, Kitakyushu, Fukuoka 8048550, Japan
[2] Daiso Co Ltd, Fine Chem Dept, Amagasaki, Hyogo 6600842, Japan
来源：
JOURNAL OF APPLIED ELECTROCHEMISTRY | 2000年 / 30卷 / 04期
关键词：
durability improvement; electrotinning line; IrO2-Ta2O5-SnO2/Ti anodes; p-phenolsulfonic acid bath;
D O I：
10.1023/A:1003977928651
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
The anodic polarization behavior and lifetime for oxygen evolution of IrO2-Ta2O5-SnO2/Ti anodes in a p-phenolsulfonic acid (PSA) solution was investigated. The oxygen overpotential of the IrO2-Ta2O5-SnO2/Ti anode was less positive potential than that of the IrO2-Ta2O5/Ti anode, although the oxygen overpotentials of both anodes were almost identical in the solution without PSA. The enhanced durability of the IrO2-Ta2O5-SnO2/Ti anode was attributed to the complete oxidizing of PSA promoted by SnO2 on anode, which resulted in the suppression of growth of the organic film originating from the PSA.
引用
收藏
页码：511 / +
页数：12
相关论文
共 50 条
  • [1] Polarization behaviour and lifetime of IrO2–Ta2O5–SnO2/Ti anodes in p-phenolsulfonic acid solutions for tin plating
    M. Morimitsu
    H. Tamura
    M. Matsunaga
    R. Otogawa
    Journal of Applied Electrochemistry, 2000, 30 : 511 - 514
  • [2] Performances of IrO2-Ta2O5SnO2/Ti anodes in p-phenolsulfonic acid bath for tin plating
    Otogawa, R
    Morimitsu, M
    Meng, H
    Tamura, H
    Matsunaga, M
    CHLOR-ALKALI AND CHLORATE TECHNOLOGY: R. B. MACMULLIN MEMORIAL SYMPOSIUM, 1999, 99 (21): : 79 - 83
  • [3] Study on the Nanostructured Ti/IrO2-Ta2O5-SnO2 Oxide Anodes
    Tang Yi
    Xu Likun
    Wang Juntao
    Xin Yonglei
    Long Ping
    RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (04) : 687 - 691
  • [4] Effect of Acid Etching on Lifetime of IrO2-Ta2O5/Ti Anodes
    Feng, Qing
    Wang, Kuaishe
    Yan, Ailing
    Hao, Xiaojun
    Jia, Bo
    Chai, Zuoqiang
    Song, Kexing
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2022, 51 (07): : 2387 - 2392
  • [5] Effect of Acid Etching on Lifetime of IrO2-Ta2O5/Ti Anodes
    Feng Qing
    Wang Kuaishe
    Yan Ailing
    Hao Xiaojun
    Jia Bo
    Chai Zuoqiang
    Song Kexing
    RARE METAL MATERIALS AND ENGINEERING, 2022, 51 (07) : 2387 - 2392
  • [6] EFFECT OF SnO2 ADDITION ON THE SERVICE LIFE AND ELECTROCHEMICAL PROPERTIES OF Ti/IrO2,+Ta2O5 ANODES IN PHENOLSULFONIC ACID SOLUTION
    J.M. Hu
    H.M. Meng
    D.B. Sun
    S.J. Zhang
    J.X. Wu and D.J. Yang Beijing Corrosion and Protection Center
    Acta Metallurgica Sinica(English Letters), 2000, (04) : 937 - 943
  • [7] Ti/IrO2-Ta2O5-SnO2纳米氧化物阳极的研究
    唐益
    许立坤
    王均涛
    辛永磊
    龙萍
    稀有金属材料与工程, 2010, 39 (04) : 687 - 691
  • [8] 添加Sn制备三元IrO2-Ta2O5-SnO2/Ti涂层（英文）
    王欣
    魏宗平
    唐电
    材料热处理学报, 2010, 31 (09) : 104 - 106
  • [9] Electrocatalytic properties of IrO2-Ta2O5/Ti coating anodes with TiN interlayer
    College of Chemical Engineering and Materials Science, Zhejiang University of Technology, Hangzhou 310032, China
    Zhongguo Youse Jinshu Xuebao, 2009, 8 (1473-1479):
  • [10] Electrooxidation using SnO2-RuO2-IrO2|Ti and IrO2-Ta2O5|Ti anodes as tertiary treatment of oil refinery effluent
    Trevino-Resendez, Jose
    Medel, Alejandro
    Cardenas, Jesus
    Meas, Yunny
    APPLIED RESEARCH, 2024, 3 (03):
12345