Improvement of the magnesium battery electrolyte properties through gamma irradiation of nano polymer electrolytes doped with magnesium oxide nanoparticles

Nanocomposite polymer electrolytes (NCPE) were prepared using nano polyethylene oxide PEO doped with Magnesium (Mg) salts. Gamma irradiation was utilized to improve the PEO-Mg salts particle sizes. Consequently, Magnesium Oxide (MgO) nanoparticles were prepared by green synthesis and incorporated into PEO-Mg salts to improve their properties toward magnesium battery electrolyte applications. The prepared samples were examined before and after exposures to the radiation doses. Dynamic light scattering (DLS) indicated the particles size of the synthesized nano polymer-Mg salts and MgO nanoparticles. Fourier transform infra-red (FTIR) spectroscopic measurements, transmission electron microscopy (TEM), electrical conductivity, electrochemical properties, and thermal stability of the samples were determined. FTIR indicated the interaction between PEO with Mg salts and MgO nanoparticles which confirmed the structure. The TEM results showed a spherical nanoparticles of MgO and a good dispersion of MgO in PEO matrix. It was found that the irradiation dose 70 kGy gave the best results for the nano polymer-Mg salts (13 nm). The electrical conductivity (sigma) evaluated for NCPE, was more than three orders of magnitude of pure PEO. The liquid NCPE of 20 mL MgO NPs at 100 kGy exhibited a maximum conductivity of 3.63 x 10(-3) Scm(-1) at room temperature. The increase in temperature caused a slight effect on conductivity, 4.85 x 10(-3) Scm(-1) at temperature 250 degrees C, at the same concentration. While un-irradiated sample of 30 mL MgO NPs (sigma) reached to 3.8 x 10(-3) Scm(-1) then became 5.03 x 10(-3) Scm(-1) by increasing temperature. From the cyclic voltammetry results, the polymer electrolytes containing MgO filler, 20 and 30 mL, for irradiated and un-irradiated samples, respectively exhibited wider electrochemical stability window than the others due to the appearance of Mg deposition/desolution peak in CV curve showed that magnesium effectively migrating through electrolytes. Thermogravimetric analysis (TGA) was enhanced by adding Mg salts electrolyte and also MgO nanoparticles to PEO. J. VINYL ADDIT. TECHNOL., 25:243-254, 2019. (c) 2018 Society of Plastics Engineers