Fatigue behaviour and life estimation of Mg/Al ultrasonic spot weld bonding welds

被引：14
|
作者：
Feng, Meng-Nan [1 ]
Chen, Yao [1 ]
Fu, Dong-Hui [2 ]
Qu, Chuan [2 ]
Luo, Zhen [1 ]
机构：
[1] Tianjin Univ, Sch Mat Sci & Engn, Tianjin 300150, Peoples R China
[2] Tianjin Univ, Sch Mech Engn, Tianjin, Peoples R China
来源：
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING | 2018年 / 23卷 / 06期
基金：
中国国家自然科学基金;
关键词：
Mg/Al dissimilar joint; ultrasonic spot weld bonding; fatigue behaviour; fatigue life estimation; fatigue fracture mode; LAP-SHEAR SPECIMENS; INTENSITY FACTOR SOLUTIONS; MAGNESIUM ALLOYS; DISSIMILAR JOINTS; MICROSTRUCTURE CHARACTERISTICS; MECHANICAL PERFORMANCE; AZ31; MAGNESIUM; ALUMINUM-ALLOY; KINKED CRACKS; STEEL SHEETS;
D O I：
10.1080/13621718.2017.1417782
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Mg/Al dissimilar joints with favourable static and dynamic mechanical properties were obtained utilising ultrasonic spot welding and ultrasonic spot weld bonding technology. The fatigue behaviour, fatigue failure mode, and typical fatigue fracture surface morphology of Mg/Al ultra-sonic spot welding and ultrasonic spot weld bonding joints were compared and observed to get a better understanding of the fatigue failure mechanism. In general, the Mg/Al ultrasonic spot weld bonding joint exhibited better fatigue performance than the ultrasonic spot welding joint. The two kinds of joints presented different fatigue failure modes with decreasing applied load level. A fatigue life prediction model was established, and the fatigue life prediction results were in good agreement with the experimental fatigue results.
引用
收藏
页码：487 / 500
页数：14
相关论文
共 50 条
  • [1] Mechanical properties and interface morphology of Mg/Al ultrasonic spot weld bonding welds
    Feng, M.
    Li, Y.
    Zhao, C.
    Luo, Z.
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2016, 21 (08) : 688 - 699
  • [2] Fatigue life estimation of ultrasonic spot welded Mg alloy joints
    Patel, V. K.
    Bhole, S. D.
    Chen, D. L.
    MATERIALS & DESIGN, 2014, 62 : 124 - 132
  • [3] Fatigue behaviour of Al/steel dissimilar resistance spot welds fabricated using Al-Mg interlayer
    Ibrahim, I.
    Ito, R.
    Kakiuchi, T.
    Uematsu, Y.
    Yun, K.
    Matsuda, C.
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2016, 21 (03) : 223 - 233
  • [4] SPOT WELDS Nondestructive Testing of Spot Welds using an Ultrasonic Resistance Spot Weld Analyzer
    Denisov, Alex
    Udzbinac, Joe
    MATERIALS EVALUATION, 2013, 71 (07) : 814 - 821
  • [5] Ultrasonic evaluation of weld strength for aluminum ultrasonic spot welds
    Ghaffari, B
    Hetrick, ET
    Mozurkewich, G
    Reatherford, LV
    Review of Progress in Quantitative Nondestructive Evaluation, Vols 24A and 24B, 2005, 760 : 1197 - 1203
  • [6] Nondestructive testing of spot welds using an ultrasonic Resistance spot weld analyzer
    Tessonics, Inc., ON, Canada
    1600, American Society for Nondestructive Testing (71):
  • [7] Improvement of fatigue life in post-weld cold worked aluminum resistant spot welds
    Kim, D.
    Blake, D. M.
    Ryu, S. J.
    Lim, B. S.
    INTERNATIONAL JOURNAL OF AUTOMOTIVE TECHNOLOGY, 2006, 7 (05) : 579 - 584
  • [8] Fatigue behaviour of dissimilar Al 5052 and Mg AZ31 resistance spot welds with Sn-coated steel interlayer
    Sun, M.
    Behravesh, S. B.
    Wu, L.
    Zhou, Y.
    Jahed, H.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2017, 40 (07) : 1048 - 1058
  • [9] FATIGUE LIFE ESTIMATION IN RESISTANCE SPOT WELDS - INITIATION AND EARLY GROWTH-PHASE
    SHEPPARD, SD
    STRANGE, M
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1992, 15 (06) : 531 - 549
  • [10] Tensile and fatigue fracture behaviour of a spot welded Al-Mg alloy
    Jiang, DM
    Kang, SB
    Kim, HW
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1997, 16 (14) : 1179 - 1181
12345