Synthesis and Characterization of Nanocrystalline ZnO Powders by a Direct Thermal Decomposition Route Using Zinc Nitrate Hexahydrate

The nanocrystalline ZnO powders were synthesized by a direct thermal decomposition using zinc nitrate hexahydrate as starting materials. The precursor was characterized by TG-DTA to determine the thermal decomposition and crystallization temperature which was found to be at 325 degrees C. The precursors were calcined at different temperatures of 400, 500, and 600 degrees C for 4 h. The structure of the prepared samples was studied by XRD, confirming the formation of wurtzite structure. The synthesized powders exhibited the UV absorption below 400 nm (3.10 eV) with a well defined absorption peak at around 285 nm (4.35 eV). The estimated direct bandgaps were obtained to be 3.19, 3.16, and 3.14 eV for the ZnO samples thermally decomposed at 400, 500, and 600 degrees C, respectively.