Phase-equilibria investigation of the Dy-Mo-Si ternary system at 1173 K (900 ° C)

被引:1
|
作者
Luo, Liying [1 ,2 ]
Wei, Chengxia [1 ,2 ]
Shu, Shi [1 ,2 ]
Zhan, Yongzhong [1 ,2 ]
机构
[1] Guangxi Univ, Coll Resources Environm & Mat, Nanning 530004, Guangxi, Peoples R China
[2] Guangxi Univ, Guangxi Key Lab Proc Nonferrous Met & Featured Ma, Nanning 530004, Guangxi, Peoples R China
基金
中国国家自然科学基金; 国家重点研发计划;
关键词
Dy-Mo-Si system; Phase equilibria; Polymorphic transformation; Solid solubility; OXIDATION RESISTANCE; RARE-EARTH; MECHANICAL-PROPERTIES; B ALLOYS; THERMODYNAMIC PROPERTIES; BEHAVIOR; BORON; MICROSTRUCTURE; MO5SI3; TI;
D O I
10.1016/j.calphad.2020.102232
中图分类号
O414.1 [热力学];
学科分类号
摘要
The phase equilibria of the Dy-Mo-Si ternary system at 1173 K (900 degrees C) was experimentally determined in the entire concentration range by using x-ray powder diffraction (XRPD), scanning electron microscope equipped with energy dispersive spectrometer (SEM-EDS), and differential scanning calorimetry (DSC). The results show that there are 13 single-phase regions, 24 two-phase regions, and 12 three-phase regions in the studied isothermal section. Nine binary compounds, i.e., alpha-MoSi2, Mo5Si3, Mo3Si, alpha-DySi2, beta-DySi1.67, Dy3Si4, DySi, Dy5Si4, and Dy5Si3 and one ternary compound Dy2Mo3Si4 were confirmed to exist at this temperature. The highest solubilities of Dy in Mo3Si and Mo in beta-DySi1.67 are both determined to be less than 1 at.%. While the solubilities of Dy in (Mo), Mo5Si3, and alpha-MoSi2 and Mo in (alpha-Dy), alpha-DySi2, Dy3Si4, DySi, Dy5Si4, and Dy5Si3 and Si in (alpha-Dy) and (Mo) are about 1-6.8 at.%. Combining both DSC analysis and XRPD results, it is concluded that the polymorphic transformation of alpha-DySi2 <->beta-DySi2 does not occur in the range of 573 K (300 degrees C) to 1323 K (1050 degrees C). DySi2 phase exists as alpha-DySi2 within the temperature range. beta-DySi2 is a metastable phase that exists in higher temperatures.
引用
收藏
页数:11
相关论文
共 50 条
  • [1] Phase Equilibria in the Fe-Mo-Ti Ternary System at 1173 K (900 A°C) and 1023 K (750 A°C)
    Knowles, A. J.
    Jones, N. G.
    Jones, C. N.
    Stone, H. J.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2017, 48A (09): : 4334 - 4341
  • [2] Phase Equilibria in the Fe-Mo-Ti Ternary System at 1173 K (900 °C) and 1023 K (750 °C)
    A. J. Knowles
    N. G. Jones
    C. N. Jones
    H. J. Stone
    Metallurgical and Materials Transactions A, 2017, 48 : 4334 - 4341
  • [3] Phase Equilibria of the Er-Si-V Ternary System at 1173 K
    Yang, Wenchao
    Zhan, Yongzhong
    Wang, Lijun
    Jiang, Wenping
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2012, 33 (04) : 288 - 292
  • [4] Phase Equilibria of the Er-Si-V Ternary System at 1173 K
    Wenchao Yang
    Yongzhong Zhan
    Lijun Wang
    Wenping Jiang
    Journal of Phase Equilibria and Diffusion, 2012, 33 : 288 - 292
  • [5] TERNARY PHASE-EQUILIBRIA IN THE ZR-SI-C SYSTEM
    WANG, YZ
    CARIM, AH
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1995, 78 (03) : 662 - 666
  • [6] Phase Equilibria of the Al-Mo-Dy Ternary System at 873 K
    Wang, Haizhou
    Zhan, Yongzhong
    Zhou, Wenbiao
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2013, 34 (04) : 322 - 327
  • [7] Phase Equilibria of the Al-Mo-Dy Ternary System at 873 K
    Haizhou Wang
    Yongzhong Zhan
    Wenbiao Zhou
    Journal of Phase Equilibria and Diffusion, 2013, 34 : 322 - 327
  • [8] Solid-state phase equilibria in the Co-Pt-Dy ternary system at 1173 K
    Gu Zhengfei
    Li Ruifeng
    Cheng Gang
    Zheng Fuqiang
    Wu Yong
    Deng Ting
    JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 504 (01) : 65 - 69
  • [9] PHASE-EQUILIBRIA IN THE NI-AL-TI SYSTEM AT 1173 K
    NASH, P
    LIANG, WW
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (03): : 319 - 322
  • [10] Phase Equilibria of the Zr-Si-Y Ternary System at 900°C
    Zhou, Xiang
    Zhao, Manxiu
    He, Xinlong
    Yin, Fucheng
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2018, 39 (06) : 882 - 890