Modulating the magnetic properties of BiFeO3 by addition of Ba5 TbTi3V7O30

xBiFeO(3)-(1-x)Ba5TbTi3V7O30 (xBFO-BTTV) ceramic composites with different x values were prepared by high temperature solid state reaction technique and sintering at 1073 K. The formation of composite structure consisting of BFO and BTTV phases was confirmed by XRD study. Surface morphology was studied by scanning electron microscope (SEM) and shows that structure with high density was obtained in the composite 0.3BFO-BTTV whereas the average grain size increases by increasing x, i.e. by increasing amount of BiFeO3 in the system. Magnetic measurements were done in a wide temperature range, i.e. from 10 to 350 K, by vibrating sample magnetometer (VSM) and showed that the magnetization changes by changing the value of x in the composite. BiFeO3 is antiferromagnetic in nature with weak ferromagnetism. Addition of Ba5TbTi3V7O30 enhances magnetic properties of the composite and maximal coercivity and remnant magnetization are obtained in the composite 0.7BFO-BTTV.