Microstructure and mechanical properties of a spark plasma sintered Ti-45Al-8.5Nb-0.2W-0.2B-0.1Y alloy

被引：59
|
作者：
Lu, X. [1 ,2 ]
He, X. B. [2 ]
Zhang, B. [3 ]
Zhang, L. [2 ]
Qu, X. H. [2 ]
Guo, Z. X. [1 ]
机构：
[1] UCL, Dept Chem, London WC1H 0AJ, England
[2] Univ Sci & Technol Beijing, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
[3] Beijing Inst Aeronaut Mat, Beijing 100095, Peoples R China
来源：
INTERMETALLICS | 2009年 / 17卷 / 10期
关键词：
Titanium aluminides; based on TiAl; Sintering; Microstructure; HIGH NB; BEHAVIOR; FRACTURE; DEFORMATION; OXIDATION;
D O I：
10.1016/j.intermet.2009.03.013
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
A high Nb containing TiAl alloy from pre-alloyed powder of Ti-45Al-8.5Nb-0.2B-0.2W-0.1Y was processed by spark plasma sintering (SPS). The effects of sintering temperature on the microstructure and mechanical properties were studied. The optimized conditions yield high densities and uniform microstructure. Specimens sintered at 1100 degrees C are characterized by fine duplex microstructure, leading to superior room temperature mechanical properties with a tensile strength of 1024 MPa and an elongation of 1.16%. Specimens sintered at 1200 degrees C are of fully lamellar microstructure with a tensile strength of 964 MPa and an elongation of 0.88%. The main fracture mode in the duplex microstructure was transgranular in the equiaxed gamma grains and interlamellar in the lamellar colonies. For the fully lamellar structure, the fracture mode was dominated by interlamellar, translamellar and stepwise failure. (C) 2009 Elsevier Ltd. All rights reserved.
引用
收藏
页码：840 / 846
页数：7
相关论文
共 50 条
  • [1] Effect of Al on Microstructures and Properties of Ti-45Al-8.5Nb-0.2B-0.2W Alloy
    Xu, Xiangjun
    Lin, Junpin
    Han, Dongdong
    HIGH PERFORMANCE STRUCTURE MATERIALS, 2013, 747-748 : 44 - 49
  • [2] B19 phase in Ti-45Al-8.5Nb-0.2W-0.2B-0.02Y alloy
    Song, L.
    Xu, X. J.
    You, L.
    Liang, Y. F.
    Lin, J. P.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 618 : 305 - 310
  • [3] Microstructure Evolution of a Ti-45Al-8.5Nb-0.2W-0.2B-0.02Y Alloy during Massive Transformation and Subsequent Annealing
    Song, Lin
    Wang, Chunqing
    Xue, Xiangyi
    Xu, Yong
    Zhang, Tiebang
    Li, Jinshan
    METALS, 2018, 8 (02)
  • [4] Microstructure Evolution of Ti-45Al-8.5Nb-0.2W-0.2B-0.02Y Alloy during Long-Term Thermal Exposure
    Chen, Zhiyuan
    Cai, Zhengkun
    Jiang, Xiaosong
    Chen, Song
    Huang, Zewen
    Sun, Hongliang
    MATERIALS, 2020, 13 (07)
  • [5] Fatigue Failure Analyses on a Ti-45Al-8Nb-0.2W-0.2B-0.1Y Alloy at Different Temperatures
    Wang, Xi-Shu
    Zhang, Min
    Song, Xi-Ping
    Jia, Su
    Chen, Qiang
    Kawagoishi, Norio
    MATERIALS, 2012, 5 (11): : 2280 - 2291
  • [6] The effect of a small addition of nickel on the sintering, sintered microstructure, and mechanical properties of Ti-45Al-5Nb-0.2C-0.2B alloy
    Qian, M., 1600, Elsevier Ltd (578):
  • [7] The effect of a small addition of nickel on the sintering, sintered microstructure, and mechanical properties of Ti-45Al-5Nb-0.2C-0.2B alloy
    Xia, Y.
    Schaffer, G. B.
    Qian, M.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 578 : 195 - 201
  • [8] STUDY ON FORMATION OF LAMELLAR MICROSTRUCTURE OF Ti-45Al-8.5Nb-0.2W-0.2B-0.02Y ALLOY BY HIGH TEMPERATURE LASER SCANNING CONFOCAL MICROSCOPE
    Xu, Xiangjun
    Xiang, Chao
    Liu, Pingping
    Quan, Xin
    HIGH TEMPERATURE MATERIAL PROCESSES, 2021, 25 (04):
  • [9] Microstructure and mechanical properties of as-cast Ti-45Al-8.5Nb-(W,B,Y) alloy with industrial scale
    Wang, Y. H.
    Lin, J. P.
    He, Y. H.
    Wang, Y. L.
    Chen, G. L.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 471 (1-2): : 82 - 87
  • [10] Effect of cooling rate on microstructure evolution of Ti-45Al-8.5Nb-0.2W-0.2B-0.02Y alloy during multi-step heat treatment
    Qiang, Fengming
    Kou, Hongchao
    Tang, Bin
    Song, Lin
    Li, Jinshan
    MATERIALS CHARACTERIZATION, 2018, 145 : 210 - 217
12345