Change of Spinel in High Ca Treament at 38CrMoAl Steel

被引：4
|
作者：
Li, Yang [1 ,2 ]
Yang, Hao [1 ]
Jiang, Zhou-Hua [1 ,2 ]
Li, Hua-Bing [1 ,2 ]
Sun, Meng [1 ]
Ma, Shuai [1 ]
机构：
[1] Northeastern Univ, Sch Met, Shenyang 110819, Liaoning, Peoples R China
[2] Northeastern Univ, State Key Lab Rolling & Automat, Shenyang 110819, Peoples R China
来源：
ISIJ INTERNATIONAL | 2022年 / 62卷 / 11期
基金：
中国国家自然科学基金;
关键词：
Ca treatment; 38CrMoAl steel; CaO; inclusions; spinel; CALCIUM-TREATMENT; NONMETALLIC INCLUSION; CLEAN STEEL; LIQUID; DEOXIDATION; DEPHOSPHORIZATION; DEFORMATION; MECHANISM; OXYGEN; OXIDE;
D O I：
10.2355/isijinternational.ISIJINT-2022-188
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
In this study, 38CrMoAl steel was treated with calcium under the pressure of 2 MPa, and four groups of high aluminum steels with the highest calcium content of 0.01% were obtained. Spinel inclusions with high MgO content, CaO and MgO inclusions with original spinel morphology were found by testing and analyzing the morphology towards composition of inclusions in the high Ca content steel. Combined with thermodynamic calculation, a Ca-Al spinel reaction model was proposed, the solid/liquid phase denaturation mechanism of calcium treated spinel was explored, and the influence of total oxygen content on phase equilibrium in denaturation process was analyzed. At last, it was obtained that the spinel denaturation products is MgO+ Spinel, CaO-Al2O3-MgO and CaO-Al2O3 when the mass fraction of calcium was low; And the spinel denaturation products with high calcium content are MgO+ Spinel, MgO and CaO.
引用
收藏
页码：2276 / 2285
页数：10
相关论文
共 50 条
  • [1] 38CrMoAl
    热处理技术与装备, 2017, (03) : 20 - 20
  • [2] LASER BORIDING OF 38CrMoAl STEEL.
    Li, Dan-ming
    Jinshu Rechuli/Heat Treatment of Metals, 1987, (09): : 16 - 20
  • [3] THE FRETTING BEHAVIOR OF A NITRIDED STEEL 38CRMOAL
    DENG, YS
    ZHANG, BY
    LUO, WL
    WEAR, 1988, 125 (1-2) : 193 - 204
  • [4] Effect of calcium treatment on inclusions in 38CrMoAl high aluminum steel
    Li, Yang
    Chen, Changyong
    Zhang, Cong
    Ma, Shuai
    Yang, Hao
    Sun, Meng
    Cao, Haibo
    Jiang, Zhouhua
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2024, 43 (01)
  • [5] 38CrMoAl钢
    热处理技术与装备, 2016, (05) : 64 - 64
  • [6] Study on composite surface treatment of 38CrMoAl steel
    董仕节
    史耀武
    范莉
    赵玉梅
    张菁
    赵宝亮
    China Welding, 2001, (01) : 70 - 74
  • [7] Microstructure of ion nitriding layer in 38CrMoAl steel
    Zhou, Shang-Qi
    Hou, Qiong
    Ren, Qin
    Jinshu Rechuli/Heat Treatment of Metals, 2002, 27 (10):
  • [8] Interaction between microporous magnesia castable and 38CrMoAl steel
    Cheng Yuan
    Yu Liu
    Guang-qiang Li
    Yong-shun Zou
    Ao Huang
    Journal of Iron and Steel Research International, 2023, 30 : 516 - 524
  • [9] Study on surface alloying of 38CrMoAl steel by electron beam
    Ren, Xulong
    Wang, Rong
    Wei, Deqiang
    Huang, Yuyan
    Zhang, Hanqing
    NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2021, 505 : 44 - 49
  • [10] Effect of Pre-corrosion on Fatigue Life of High Strength Steel 38CrMoAl
    刘建华
    Journal of Wuhan University of Technology(Materials Science Edition), 2011, 26 (04) : 648 - 653
12345