Inducing tunable host luminescence in Zn2GeO4 tetrahedral materials via doping Cr3+

Zn2GeO4 consisting of tetrahedron, and it is a self-luminescent material due to the presence of the native defects and shows a bluish white emission excited by ultraviolet. Although Cr3+ doped in a tetrahedron generally cannot show luminescence, in this research, new defects are formed as Cr3+ doped in Zn2GeO4, hence a green emission band can be obtained. Meanwhile, the intensity of host emission is also decreased. Therefore, Zn2GeO4:Cr3+ are synthesized using a high-temperature solid-phase method. Thermoluminescence (TL) and luminescence decay curves are used to investigate the variation of native defects. The emission colour can be tuned from bluish white to green when Cr3+ doped in Zn2GeO4. This result has guidance for controlling the native emission of self-luminescent material. (C) 2018 Elsevier B.V. All rights reserved.