Characterization of high-strength high-nitrogen austenitic stainless steel synthesized from nitrided powders by spark plasma sintering

被引:38
|
作者
Hu, Ling [1 ,2 ]
Peng, Hanlin [2 ,3 ]
Baker, Ian [2 ]
Li, Liejun [1 ]
Zhang, Weipeng [1 ]
Ngai, Tungwai [1 ]
机构
[1] South China Univ Technol, Natl Engn Res Ctr Near Net Shape Forming Technol, Guangzhou 510640, Guangdong, Peoples R China
[2] Dartmouth Coll, Thayer Sch Engn, Hanover, NH 03755 USA
[3] Huazhong Univ Sci & Technol, Sch Mat Sci & Engn, State Key Lab Mat Proc & & Mould Technol, Wuhan 430074, Hubei, Peoples R China
关键词
High-N austenitic stainless steel; Nitriding; Nitride precipitate; XPS; Strengthening mechanisms; HEAT-TREATMENT; DISCONTINUOUS PRECIPITATION; MECHANICAL-PROPERTIES; TEMPERATURE; CHROMIUM; XPS; MICROSTRUCTURE; BEHAVIORS; CARBIDES; CR2N;
D O I
10.1016/j.matchar.2019.04.005
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A high-N austenitic stainless steel (HNASS) was fabricated using a novel approach, in which duplex stainless steel powders were firstly gas nitrided in the temperature range of 700-900 degrees C and then consolidated using spark plasma sintering, resulting in an FCC matrix with average grain sizes of 1.6-8.2 mu m. The Cr2N precipitates transformed from cellular precipitates (lamellar within the grains) to intergranular precipitation (equiaxed along the grain boundaries) as the nitriding temperature rose from 700 degrees C to 750 degrees C, and the N content rose from 0.68 wt% to 1.71 wt%. The 700 degrees C-treated alloy exhibits a yield strength of 783 MPa, a high tensile strength of 1091 MPa, and an elongation of 41% while the 900 degrees C-treated alloy exhibits an ultra-high compressive strength of 3017 MPa, and hardness of 520 HV. These values dramatically exceed the published values of similar HNASSs. Quantitative calculations showed that these superior mechanical properties could be attributed to increased solid solution and grain boundary strengthening. Furthermore, it can be inferred that while the equiaxed Cr2N phase increased the yield strength, it greatly degraded the fracture toughness.
引用
收藏
页码:76 / 84
页数:9
相关论文
共 50 条
  • [1] High-strength austenitic stainless steel
    V. G. Gavrilyuk
    H. Berns
    Metal Science and Heat Treatment, 2007, 49 : 566 - 568
  • [2] High-strength austenitic stainless steel
    Gavrilyuk, V. G.
    Berns, H.
    METAL SCIENCE AND HEAT TREATMENT, 2007, 49 (11-12) : 566 - 568
  • [3] Deformation twinning in high-nitrogen austenitic stainless steel
    Lee, T.-H.
    Oh, C.-S.
    Kim, S.-J.
    Takaki, S.
    ACTA MATERIALIA, 2007, 55 (11) : 3649 - 3662
  • [4] High-nitrogen austenitic stainless steels with high strength and corrosion resistance
    Rhodes, GO
    Conway, JJ
    JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY, 1996, 48 (04): : 28 - 31
  • [5] Fatigue and corrosion fatigue of high-nitrogen austenitic stainless steel
    Diener, M
    Speidel, MO
    MATERIALS AND MANUFACTURING PROCESSES, 2004, 19 (01) : 111 - 115
  • [6] Aging precipitation and recrystallization in high-nitrogen austenitic stainless steel
    石锋
    王立军
    崔文芳
    祁阳
    刘春明
    Transactions of Nonferrous Metals Society of China, 2009, 19(S3) (S3) : 569 - 572
  • [7] Aging precipitation and recrystallization in high-nitrogen austenitic stainless steel
    Shi Feng
    Wang Li-jun
    Cui Wen-fang
    Qi Yang
    Liu Chun-ming
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2009, 19 : S569 - S572
  • [8] Grain boundary engineering of high-nitrogen austenitic stainless steel
    Kokawa, H.
    Jin, W. Z.
    Wang, Z. J.
    Michiuchi, M.
    Sato, Y. S.
    Dong, W.
    Katada, Y.
    THERMEC 2006, PTS 1-5, 2007, 539-543 : 4962 - +
  • [9] High-cycle fatigue behavior of high-nitrogen austenitic stainless steel
    Dai, Qixun
    Yuan, Zhizhong
    Chen, Xi
    Chen, Kangmin
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 517 (1-2): : 257 - 260
  • [10] HIGH-STRENGTH AUSTENITIC STAINLESS STEEL FOR CRYOGENIC SERVICE
    SPAEDER, CE
    MAJETICH, JC
    BRICKNER, KG
    METALS ENGINEERING QUARTERLY, 1969, 9 (03): : 1 - &