Effect of Co and Ni on the corrosion behavior of low alloy steels in wet/dry environments

被引:206
|
作者
Nishimura, T [1 ]
Katayama, H [1 ]
Noda, K [1 ]
Kodama, T [1 ]
机构
[1] Natl Res Inst Met, Frontier Res Ctr Struct Mat, Tsukuba, Ibaraki 3050047, Japan
关键词
low alloy steel; EIS; TEM; atmospheric corrosion; rust;
D O I
10.1016/S0010-938X(00)00018-4
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The iron rust phase formed on low alloy steels has been analyzed by using EPMA, XPS, TEM and alternating current (AC) impedance methods after wet/dry corrosion tests using 0.5 mass% NaCl solution. Steel containing Co or Ni from 1 to 3 mass% showed higher corrosion resistance than carbon steel in the test. Cobalt was identified in its trivalent state (Co3+) in the rust of Co-bearing steel by EPMA and TEM, which means that Co was incorporated mainly into FeOOH. On the other hand, nickel was identified in its bivalent state (Ni2+) in the rust of Ni-bearing steel by XPS and TEM, which implies that Ni was involved in the formation of spinel oxide in rust. AC impedance demonstrated that the resistance of rust (R-rust) corresponds to the structural factor of the rust. The high value of R-rust for Co-bearing steel indicated high resistance of FeOOH-type rust against the penetration of Cl ion. The high R-rust value was observed at the early stage of corrosion cycles. The R-rust value of Ni-bearing steel increased as the amount of rust on the steel increased, implying that Ni helped to convert spinels into a dense and fine structure, and that its effectiveness increased after the formation of the inner rust layer. (C) 2000 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码:1611 / 1621
页数:11
相关论文
共 50 条
  • [1] Effect of Al on the corrosion behavior of low alloy steels in wet/dry environment
    Nishimura, T
    Tahara, A
    Kodama, T
    MATERIALS TRANSACTIONS, 2001, 42 (03) : 478 - 483
  • [2] Effect of Al on the corrosion behavior of low alloy steels in wet/dry environment
    Nishimura, T
    Tahara, A
    Kodama, T
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2000, 64 (02) : 148 - 153
  • [3] Effect of Co and Ni on the electrochemical behavior of rust formed on the low alloy steels in cyclic wet and dry environment
    Nishimura, T
    Katayama, H
    Noda, K
    Kodama, T
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2000, 86 (02): : 111 - 115
  • [4] Corrosion behavior of low alloy steels in a wet–dry acid humid environment
    Qing-he Zhao
    Wei Liu
    Jian-wei Yang
    Yi-chun Zhu
    Bin-li Zhang
    Min-xu Lu
    International Journal of Minerals, Metallurgy, and Materials, 2016, 23 : 1076 - 1086
  • [5] Corrosion behavior of low alloy steels in a wet–dry acid humid environment
    Qing-he Zhao
    Wei Liu
    Jian-wei Yang
    Yi-chun Zhu
    Bin-li Zhang
    Min-xu Lu
    International Journal of Minerals Metallurgy and Materials, 2016, 23 (09) : 1076 - 1086
  • [6] Effect of sodium chloride on corrosion behavior of low-alloy steels under wet and dry condition
    Nishimura, T
    Kodama, T
    Kurosawa, K
    CORROSION AND CORROSION CONTROL IN SALTWATER ENVIRONMENTS, 2000, 99 (26): : 87 - 96
  • [7] Corrosion behavior of low alloy steels in a wet-dry acid humid environment
    Zhao, Qing-he
    Liu, Wei
    Yang, Jian-wei
    Zhu, Yi-chun
    Zhang, Bin-li
    Lu, Min-xu
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2016, 23 (09) : 1076 - 1086
  • [8] Comparative Study of Ni effect on the Corrosion Behavior of Low Alloy Steels in FGD and Acid Rain Environments
    Han, Jun-Hee
    Nguyen, Dang-Nam
    Jang, Young-Wook
    Kim, Jung-Gu
    JOURNAL OF THE KOREAN INSTITUTE OF METALS AND MATERIALS, 2009, 47 (09): : 558 - 566
  • [9] The influence of Ni alloying on corrosion behaviour of low alloy steels under wet/dry cyclic conditions
    Chen, X.
    Dong, J.
    Han, E.
    Ke, W.
    CANADIAN METALLURGICAL QUARTERLY, 2007, 46 (02) : 195 - 205
  • [10] Effect of Small Content of Chromium on Wet–Dry Acid Corrosion Behavior of Low Alloy Steel
    Qing-He Zhao
    Wei Liu
    Yi-Chun Zhu
    Bin-Li Zhang
    Shuan-Zhu Li
    Min-Xu Lu
    Acta Metallurgica Sinica(English Letters), 2017, 30 (02) : 164 - 175