Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 2. Fatigue test results and damage mechanisms

被引：10
|
作者：
Bezazi, A. [1 ]
El Mahi, A. [2 ]
Berthelot, J. -M. [3 ]
Bezzazi, B. [4 ]
机构：
[1] Univ Bristol, Dept Aerosp Engn, Bristol, Avon, England
[2] Univ Maine, F-72017 Le Mans, France
[3] Inst Adv Mat & Mech, ISMANS, Le Mans, France
[4] Univ Boumerdes, LMCC, Boumerdes, Algeria
来源：
STRENGTH OF MATERIALS | 2009年 / 41卷 / 03期
关键词：
polyvinyl chlorid; sandwich composite panels; stuff; three-point bending; damage mechanism; cyclic life criterion;
D O I：
10.1007/s11223-009-9131-6
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The analysis of stiffness degradation and the identification of damage mechanisms during and after fatigue tests of sandwich panels with PVC foam cores have been performed. The sandwich panels with cross-ply laminates skins made of glass fiber and epoxy resin were manufactured by vacuum moulding and subjected to three-point bending tests. Two PVC cores of similar type but with differing densities were investigated. The effect of core density and thickness on the damage behavior was highlighted. Using the cyclic life criterion, fatigue curves were plotted according to two models and compared with those of the literature. It has been demonstrated that the sandwich SD 2, with the higher core density, withstands a higher load and possesses greater rigidity in static tests, combined with an enhanced fatigue resistance, when compared to sandwich SD 1 which has a lower core density.
引用
收藏
页码：257 / 267
页数：11
相关论文
共 40 条
  • [1] Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 2. Fatigue test results and damage mechanisms
    A. Bezazi
    A. El Mahi
    J.-M. Berthelot
    B. Bezzazi
    Strength of Materials, 2009, 41 : 257 - 267
  • [2] Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies
    Bezazi A.
    Mahi A.
    Berthelot J.-M.
    Bezzazi B.
    Strength of Materials, 2007, 39 (2) : 170 - 177
  • [3] Failure behavior and damage model of composite sandwich panels under three-point bending fatigue load
    Dong, Fan
    Li, Yazhi
    Qi, Xin
    Ma, Weijie
    Zhou, Chunping
    Li, Biao
    THIN-WALLED STRUCTURES, 2024, 205
  • [4] EXPERIMENTAL INVESTIGATION OF THE MECHANICAL BEHAVIOR OF HONEYCOMB SANDWICH COMPOSITE UNDER THREE-POINT BENDING FATIGUE
    Mzad, Hocine
    MATERIALS PHYSICS AND MECHANICS, 2022, 48 (02): : 217 - 231
  • [5] Collapse mechanisms of sandwich beams with composite faces and a foam core, loaded in three-point bending. Part II: experimental investigation and numerical modelling
    Steeves, CA
    Fleck, NA
    INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2004, 46 (04) : 585 - 608
  • [6] The effect of delamination on damage behavior of composite laminates subjected to three-point bending
    Tang, J.
    Xing, S. L.
    Xiao, J. Y.
    Wu, Z. H.
    Wen, S. W.
    Ju, S.
    ADVANCES IN ENGINEERING MATERIALS AND APPLIED MECHANICS, 2016, : 599 - 607
  • [7] Research on three-point bending fatigue life and damage mechanism of aluminum foam sandwich panel
    Xiao, Wei
    Wang, Huihui
    Song, Xuding
    STEEL AND COMPOSITE STRUCTURES, 2024, 51 (01): : 53 - 61
  • [8] A multi-area fatigue damage model of composite honeycomb sandwich panels under three-point bending load
    Ma, Mingze
    Yao, Weixing
    Jiang, Wen
    Jin, Wei
    Chen, Yan
    Li, Piao
    COMPOSITE STRUCTURES, 2021, 261
  • [9] Experimental and Numerical Analysis of Progressive Damage of SiCf/SiC Composite under Three-Point Bending
    Li, Xiang
    Luo, Ruiying
    CRYSTALS, 2022, 12 (05)
  • [10] Fatigue behavior and damage of composite laminates under 3 point bending test
    Khelifa, Noureddine
    Bey, Kamel
    Chemami, Abdennacer
    MATERIAUX & TECHNIQUES, 2016, 104 (02):
1234