Processing and mechanical performance of 3D Cf/SiCN composites prepared by polymer impregnation and pyrolysis

The processing of 3D carbon fiber reinforced SiCN ceramic matrix composites prepared by polymer impregnation and pyrolysis (PIP) route was improved, and factors that determined the mechanical performance of the resulting composites were discussed. 3D C-f/SiCN composites with a relative density of similar to 81% and uniform microstructure were obtained after 6 PIP cycles. The optimum bending strength, Young's modulus and fracture toughness of the composites were 75.2 MPa, 66.3 GPa and 1.65 MPa m(1/2), respectively. The residual strength retention rate of the as-pyrolyzed composites was 93.3% after thermal shock test at Delta T = 780 degrees C. It further degraded to 14.6% when the thermal shock temperature difference reached to 1180 degrees C. The bending strength of the composites was 35.6 MPa after annealing at 1000 degrees C in static air. The deterioration of the bending strength should be attributed to the strength degradation of carbon fibers and decomposition of interfacial structure.