Compression After Impact Load Prediction in Graphite Epoxy Laminates

被引：0

作者：

Gunasekera, Anthony M. ^{[1
]}

机构：

[1] Embry Riddle Aeronaut Univ, Dept Aerosp Engn, Daytona Beach, FL 32114 USA

来源：

MATERIALS EVALUATION | 2010年 / 68卷 / 08期

关键词：

D O I：

暂无

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

(Edited Abstract)

引用

页码：881 / 886

页数：6

共 50 条

[1] LOAD DAMAGE IN GRAPHITE EPOXY LAMINATES
不详
ADVANCED MATERIALS & PROCESSES, 1992, 142 (06): : 43 - 44
[2] COMPRESSION FAILURES OF DAMAGED GRAPHITE EPOXY LAMINATES
JONES, R
BROUGHTON, W
MOUSLEY, RF
POTTER, RT
COMPOSITE STRUCTURES, 1985, 3 (02) : 167 - 186
[3] Failure prediction of graphite/epoxy laminates with induced intermittent load surge during fatigue
Kedlaya, DN
Pelegri, AA
ACTA MATERIALIA, 2002, 50 (19) : 4813 - 4821
[4] COMPRESSION FATIGUE BEHAVIOR OF NOTCHED GRAPHITE/EPOXY LAMINATES
ISHIKAWA, H
INTERNATIONAL JOURNAL OF FRACTURE, 1985, 27 (02) : R51 - R54
[5] DESIGNING FOR TOLERANCE TO IMPACT DAMAGE AT FASTENER HOLES IN GRAPHITE EPOXY LAMINATES UNDER COMPRESSION
JANARDHANA, MN
BROWN, KC
JONES, R
THEORETICAL AND APPLIED FRACTURE MECHANICS, 1986, 5 (01) : 51 - 55
[6] Influence of Cenosphere on Compression After Impact Strength of Glass Epoxy Laminates
Rajendran, Balaji
Kumar, Dinesh P. K.
ENGINEERING RESEARCH EXPRESS, 2021, 3 (04):
[7] MATRIX CRACKING AND DELAMINATION PREDICTION IN GRAPHITE EPOXY LAMINATES
JEN, KC
SUN, CT
JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1992, 11 (10) : 1163 - 1175
[8] STRENGTH OF NOTCHED AND UNNOTCHED GRAPHITE EPOXY LAMINATES LOADED IN COMPRESSION
ERIKSSON, I
JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1991, 10 (03) : 222 - 255
[9] Low velocity impact and compression after impact tests on thin carbon/epoxy laminates
Ghelli, Daniele
Minak, Giangiacomo
COMPOSITES PART B-ENGINEERING, 2011, 42 (07) : 2067 - 2079
[10] Compression and hydrothermal ageing after impact of carbon fibre reinforced epoxy laminates
Caldwell, Rowan L.
Davies, Peter
Arhant, Mael
Prusty, B. Gangadhara
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2024, 184

← 1 2 3 4 5 →