Synthesis, Electrical Conductivity, Spectral and Thermal Stability Studies on Poly(aniline-co-o-nitroaniline)

o-Nitroaniline units were incorporated in the polyaniline backbone through copolymerization with aniline. The copolymers were synthesized for 1:3 and 1:1 molar ratios of aniline and o-nitroaniline in acidic medium using potassium persulphate as oxidant and their properties were compared with that of polyaniline. The polymers showed less electrical conductivity than polyaniline. Unlike polyaniline, the presence of nitro group caused higher frequency dependence of electrical conductivity. Electronic spectra showed a blue shift in both the band of the copolymers due to the decrease in the extent of conjugation leading to lower conductivity, which could also be explained in terms of a decrease of delocalization of electron as evinced from electron para magnetic resonance (EPR) data. Thermo gravimetric analysis (TGA) revealed that copolymer derived from 1:1 molar ratio showed comparable thermal stability with polyaniline and the one derived from 1:3 molar ratios is thermally less stable than polyaniline. Activation energies for thermal degradation were estimated using Broido equation. The temperature dependence of electrical conductivity suggested charge transport is mainly through variable range hopping.