The Influence of Thermal-Compression Treatment under Argon Pressure of 3.0 MPa on Microstructure of Standard (Ti, W)C-WC-10Co Hardmetal

被引：4

作者：

Prokopiv, N. M. ^{[1
]}

Kharchenko, O. V.

Tkach, S. V.

Vasilenko, L. E.

Prokopiv, N. N.

Serdyuk, Yu. D.

Semizhon, O. A.

机构：

[1] Natl Acad Sci Ukraine, Bakul Inst Superhard Mat, UA-04074 Kiev, Ukraine

来源：

JOURNAL OF SUPERHARD MATERIALS | 2011年 / 33卷 / 05期

关键词：

hardmetal; cutting inserts; thermal-compression treatment; pressure; argon; structure; porosity; carbides; cobalt; Fourier analysis;

D O I：

10.3103/S1063457611050066

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The paper provides results of comparative investigations including microstructure analysis and Fourier analysis of structure of (Ti, W)C-WC-10Co hardmetal prior to and after thermal-compression treatment under argon pressure of 3.0 MPa at temperature of 1480 degrees C and isothermal holding for 20 min.