Hierarchical sheet-on-sheet heterojunction array of a β-Ni(OH)2/Fe(OH)3 self-supporting anode for effective overall alkaline water splitting

Rationally designing high-performance non-noble metal electrocatalysts is of essence to improve energy conversion efficiency in water splitting. Herein, a unique 3D hierarchical sheet-on-sheet heterojunction between Fe(OH)(3) and beta-Ni(OH)(2) on pretreated Ni foam (NiFe-HD/pre-NF) was fabricated by a two-step strategy involving the interfacial hydrolysis-deposition of Fe2+ and electrodeposition of Ni2+. The presence of the Ni-O-Fe bridge at the Fe(OH)(3)/beta-Ni(OH)(2) heterointerface can induce interfacial electronic redistribution to form Ni3+ in NiFe-HD/pre-NF, and further strengthen the adsorption of OH- and weaken the O-H bond to change the rate-determining step (RDS) for accelerating OER kinetics. Benefiting from the sheet-on-sheet architecture and dual-phase synergism on NiFe-HD/pre-NF, the optimal NiFe-HD/pre-NF exhibits excellent OER performance with a lower overpotential of 256 mV at 100 mA cm(-2), a small Tafel slope of 81 mV dec(-1), high intrinsic activity and robust stability. Alkaline water-splitting using NiFe-HD/pre-NF as the anode requires ultralow cell voltages of 1.62 V and 1.83 V at current densities of 100 mA cm(-2) and 400 mA cm(-2), respectively, which are comparable with commercial alkaline water electrolysis, and operates steadily at a current density of 100 mA cm(-2) for 85 h without decay. This work proposes a facile strategy for constructing heterojunctions and modulating electronic interaction to develop electrocatalysts with new architectures.