Role of water chemistry and microstructure in stress corrosion cracking in the fusion boundary region of an Alloy 182-A533B low alloy steel dissimilar weld joint in high temperature water

被引：73
|
作者：
Peng, Qunjia [1 ,2 ]
Xue, He [3 ]
Hou, Juan [1 ]
Sakaguchi, Kazuhiko [1 ]
Takeda, Yoichi [1 ]
Kuniya, Jiro [1 ]
Shoji, Tetsuo [1 ]
机构：
[1] Tohoku Univ, Fracture & Reliabil Res Inst, Grad Sch Engn, Aoba Ku, Sendai, Miyagi 9808579, Japan
[2] Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China
[3] Xian Univ Sci & Technol, Sch Mech Engn, Xian 710054, Peoples R China
来源：
CORROSION SCIENCE | 2011年 / 53卷 / 12期
关键词：
Low alloy steel; Alloy; SEM; TEM; Stress corrosion; Welding; ENVIRONMENTALLY-ASSISTED CRACKING; NICKEL-BASE ALLOYS; STAINLESS-STEEL; SUSCEPTIBILITY; PROPERTY;
D O I：
10.1016/j.corsci.2011.08.046
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Stress corrosion cracking (SCC) in the fusion boundary (FB) region of an Alloy 182-low alloy steel (LAS) dissimilar weld joint in 288 C water was investigated by experiments and finite element simulation. Creviced bent beam and crack growth rate (CGR) experiments showed that, while the FB was a barrier to SCC growth, further crack growth into LAS was activated by a combined effect of sulfate and dissolved oxygen in water. Finite element simulation suggested that a positive gradient of hardness as the crack approached to the FB in dilution zone caused decreased CGR. Role of microstructure and water chemistry in SCC was discussed. (C) 2011 Elsevier Ltd. All rights reserved.
引用
收藏
页码：4309 / 4317
页数：9
相关论文
共 50 条
  • [1] Microstructure and stress corrosion cracking of the fusion boundary region in an alloy 182-A533B low alloy steel dissimilar weld joint
    Hou, Juan
    Peng, Qunjia
    Takeda, Yoichi
    Kuniya, Jiro
    Shoji, Tetsuo
    CORROSION SCIENCE, 2010, 52 (12) : 3949 - 3954
  • [2] STRESS CORROSION CRACKING BEHAVIOR NEAR THE FUSION BOUNDARY OF DISSIMILAR WELD JOINT WITH ALLOY 182-A533B LOW ALLOY STEEL
    Abe, Hiroshi
    Ishizawa, Makoto
    Watanabe, Yutaka
    15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 791 - 802
  • [3] Microstructure and mechanical property of the fusion boundary region in an Alloy 182-low alloy steel dissimilar weld joint
    Hou, J.
    Peng, Q. J.
    Takeda, Y.
    Kuniya, J.
    Shoji, T.
    Wang, J. Q.
    Han, E. -H.
    Ke, W.
    JOURNAL OF MATERIALS SCIENCE, 2010, 45 (19) : 5332 - 5338
  • [4] Microstructure and mechanical property of the fusion boundary region in an Alloy 182-low alloy steel dissimilar weld joint
    J. Hou
    Q. J. Peng
    Y. Takeda
    J. Kuniya
    T. Shoji
    J. Q. Wang
    E.-H. Han
    W. Ke
    Journal of Materials Science, 2010, 45 : 5332 - 5338
  • [5] Stress Corrosion Cracking Behavior in the Transition Region of Alloy 182/Low-Alloy Reactor Pressure Vessel Steel Dissimilar Metal Weld Joints in Light Water Reactor Environments
    Seifert, Hans-Peter
    Ritter, Stefan
    Leber, Hans J.
    Roychowdhury, Supratik
    CORROSION, 2015, 71 (04) : 433 - 454
  • [6] Effects of electropolishing on corrosion and stress corrosion cracking of Alloy 182 in high temperature water
    Han, Yaolei
    Han, En-Hou
    Peng, Qunjia
    Ke, Wei
    CORROSION SCIENCE, 2017, 121 : 1 - 10
  • [7] Primary water stress corrosion cracking behavior of an Alloy 600/182 weld
    Lim, Yun Soo
    Hwang, Seong Sik
    Kim, Sung Woo
    Kim, Hong Pyo
    CORROSION SCIENCE, 2015, 100 : 12 - 22
  • [8] Effect of heat treatment on grain boundary carbides and primary water stress corrosion cracking resistance of Alloy 182 weld
    Kim, Ho-Sub
    Chen, Junjie
    Lee, Hyeon Bae
    Shin, Ji Ho
    Kong, Byeong Seo
    Oh, Seungjin
    Jang, Hun
    Jang, Changheui
    CORROSION SCIENCE, 2021, 191
  • [9] Compared Modeling Study of Primary Water Stress Corrosion Cracking at Dissimilar Weld of Alloy 182 of Pressurized Water Nuclear Reactor According to Hydrogen Concentration
    Aly, Omar F.
    Neto, Miguel M.
    Schvartzman, Monica M. A. M.
    Lima, Luciana I. L.
    JOURNAL OF DISASTER RESEARCH, 2015, 10 (04) : 641 - 646
  • [10] STRESS-CORROSION CRACKING OF ALLOY-600 AND ALLOY-690 AND NO-82 AND NO-182 WELD METALS IN HIGH-TEMPERATURE WATER
    PAGE, RA
    CORROSION, 1983, 39 (10) : 409 - 421
12345