Influence of molar ratio in aminoplastic resins on the dependence of the measured perforator values on the moisture content of wood-based panels

被引：4
|
作者：
Johnsson, B. [2 ]
Engstrom, B. [2 ]
Roffael, E. [1 ]
机构：
[1] Univ Gottingen, D-37077 Gottingen, Germany
[2] Casco Adhes AB, S-85013 Sundsvall, Sweden
来源：
WOOD SCIENCE AND TECHNOLOGY | 2011年 / 45卷 / 02期
关键词：
FORMALDEHYDE;
D O I：
10.1007/s00226-011-0411-5
中图分类号：
S7 [林业];
学科分类号：
0829 ; 0907 ;
摘要：
The correction factor developed by Jann and Deppe (1990) to adjust the measured perforator values of particleboards and fibreboards measured at different moisture contents in the range of 3% a parts per thousand currency sign u a parts per thousand currency sign 9% to the level at 6.5% moisture content has two main deficiencies. It takes no account of the influence of the molar ratio of the resins used, which seems to remarkably impact the relationship between the moisture content and the measured perforator values. Moreover, research work revealed that the correction factor to be applied also depends on the moisture content, at which the perforator value was measured, according to an inversely proportional correlation. Besides, the correction factor according to Jann-Deppe leaves this fact unconsidered.
引用
收藏
页码：389 / 398
页数：10
相关论文
共 12 条
  • [1] Influence of molar ratio in aminoplastic resins on the dependence of the measured perforator values on the moisture content of wood-based panels
    B. Johnsson
    B. Engström
    E. Roffael
    Wood Science and Technology, 2011, 45 : 389 - 398
  • [2] On the influence of binder content in particleboards bonded with resins of high and low molar ratio on the formaldehyde release measured by the perforator method
    Roffael, E.
    Behn, C.
    EUROPEAN JOURNAL OF WOOD AND WOOD PRODUCTS, 2012, 70 (06) : 819 - 822
  • [3] Influence of moisture on stress-wave properties of wood-based panels
    Wu, QL
    PROCEEDINGS OF THE ELEVENTH INTERNATIONAL SYMPOSIUM ON NONDESTRUCTIVE TESTING OF WOOD, 1999, : 19 - 26
  • [4] THE INFLUENCE OF UREA FORMALDEHYDE RESINS ON PYROLYSIS CHARACTERISTICS AND PRODUCTS OF WOOD-BASED PANELS
    Feng, Yongshun
    Mu, Jun
    Chen, Shihua
    Huang, Zhiyi
    Yu, Zhiming
    BIORESOURCES, 2012, 7 (04): : 4600 - 4613
  • [5] Influence of Moisture Content on the Mechanical Properties of Selected Wood-based Composites
    Sala, Conrad M.
    Robles, Eduardo
    Gumowska, Aneta
    Wronka, Anita
    Kowaluk, Grzegorz
    BIORESOURCES, 2020, 15 (03) : 5503 - 5513
  • [6] Influence of temperature and moisture content on the thermal conductivity of wood-based fibreboards
    Troppova, Eva
    Svehlik, Matej
    Tippner, Jan
    Wimmer, Rupert
    MATERIALS AND STRUCTURES, 2015, 48 (12) : 4077 - 4083
  • [7] Influence of temperature and moisture content on the thermal conductivity of wood-based fibreboards
    Eva Troppová
    Matěj Švehlík
    Jan Tippner
    Rupert Wimmer
    Materials and Structures, 2015, 48 : 4077 - 4083
  • [8] Measurements of sorption isotherms of selected commercial wood-based panels and predictions of moisture content changes in service
    Sekino, N
    Suematsu, A
    Kohrai, H
    Yasui, E
    MOKUZAI GAKKAISHI, 1999, 45 (03): : 237 - 243
  • [9] Measurements of sorption isotherms of selected commercial wood-based panels and predictions of moisture content changes in service
    Sekino, Noboru
    Suematsu, Atsuhiko
    Kohrai, Hideaki
    Yasui, Etsuya
    Mokuzai Gakkaishi/Journal of the Japan Wood Research Society, 1999, 45 (03): : 237 - 243
  • [10] On the influence of binder content in particleboards bonded with resins of high and low molar ratio on the formaldehyde release measured by the perforator methodEinfluss des Bindemittelgehalts in Spanplatten auf den Perforatorwert in Abhängigkeit vom Molverhältnis des verwendeten Harzes
    E. Roffael
    C. Behn
    European Journal of Wood and Wood Products, 2012, 70 : 819 - 822
12