Effect of Solution Heat Treatment Time on a Rheocast Al-Zn-Mg-Cu Alloy

被引：10
|
作者：
Mazibuko, Nonjabuliso E. [1 ]
Curle, Ulyate A. [1 ]
机构：
[1] CSIR, ZA-0001 Pretoria, South Africa
来源：
LIGHT METALS TECHNOLOGY V | 2011年 / 690卷
关键词：
CSIR-RCS; eutectic phase; intermetallic phases; hardness; EVOLUTION;
D O I：
10.4028/www.scientific.net/MSF.690.343
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
During rheo-high pressure die casting (R-HPDC) of Al-Zn-Mg-Cu alloys a coarse eutectic phase is formed. This eutectic phase is difficult to take into solution because of its size and it would require longer solution heat treatment times. The objective of this work was to determine the time for sufficient dissolution of the eutectic phase in this Al-Zn-Mg-Cu alloy. Solution heat treatment was carried out at 473 degrees C for various time periods and the samples were quenched in water. The samples were then artificially aged at 120 degrees C for 24 hrs. A component of the eutectic was observed to have dissolved and another component transformed to new intermetallic phases for all solution heat treatment times at 473 degrees C.
引用
收藏
页码：343 / 346
页数：4
相关论文
共 50 条
  • [1] Heat treatment of bulk nanocrystalline Al-Zn-Mg-Cu alloy
    Chen, Han-Bin
    Cheng, Jun-Sheng
    Yang, Bin
    Zhang, Ji-Shan
    Fan, Jian-Zhong
    Tian, Xiao-Feng
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2007, 17 (01): : 30 - 34
  • [2] Effect of recrystallization and heat treatment on strength and SCC of an Al-Zn-Mg-Cu alloy
    Chen, Songyi
    Chen, Kanghua
    Dong, Pengxuan
    Ye, Shengping
    Huang, Lanping
    JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 581 : 705 - 709
  • [3] Effect of heat treatment on microstructure and mechanical properties of a novel Al-Zn-Mg-Cu alloy
    Yang, Yan-mei
    Tang, Xin-chen
    Li, Ye-fei
    Fang, Xue-wei
    Yi, Da-wei
    Zhang, Zhi-yun
    Zheng, Qiao-ling
    Wang, Zhi-xi
    Zhang, Guo-yu
    Zhang, Su
    Cheng, Hao
    He, Yang
    Liu, Yi-bo
    Wu, Zi-han
    Chen, Ya-nan
    Gao, Yi-min
    CHINA FOUNDRY, 2025,
  • [4] Effect of heat treatment on microstructure, hardening and plasticity of a commercial Al-Zn-Mg-Cu alloy
    Chemingui, Mahmoud
    Benkhenafou, Fethi
    Khitouni, Mohamed
    Jozwiak, Karol
    Mesmacque, Gerard
    Shi, MingQuan
    Douadji, Lyes
    INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2018, 109 (12) : 1113 - 1121
  • [5] Electrochemical assessment of laser heat treatment of an Al-Zn-Mg-Cu alloy
    Wang, Kaining
    Su, Ruiming
    Liu, Tong
    Qu, Yingdong
    Li, Rongde
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2020, 71 (03): : 374 - 381
  • [6] Effect of temperature-incremental solution heat treatment on the microstructure and mechanical properties of Al-Zn-Mg-Cu alloy
    2000, Central South University of Technology, China (31):
  • [7] Effect of heat treatment on microstructures and mechanical properties of a bulk nanostructured Al-Zn-Mg-Cu alloy
    Han-bin Chen1
    International Journal of Minerals Metallurgy and Materials, 2009, 16 (06) : 672 - 676
  • [8] Effect of heat treatment on microstructures and properties of a novel Al-Zn-Mg-Cu alloy for oil drilling
    Fu, Yanjun
    Li, Xiwu
    Wen, Kai
    Huang, Shuhui
    Dong, Yang
    Rao, Mao
    Yang, Fubo
    Wang, Yugang
    Xiong, Baiqing
    Li, Zhihui
    PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2019, 29 (02) : 217 - 223
  • [9] Effect of Thermomechanical Treatment on Microstructure and Properties of Al-Zn-Mg-Cu Alloy
    Zhang, Weijian
    Su, Ruiming
    Li, Guanglong
    Qu, Yingdong
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2025, 78 (05)
  • [10] Effect of heat treatment on microstructures and mechanical properties of a bulk nanostructured Al-Zn-Mg-Cu alloy
    Chen, Han-bin
    Yang, Bin
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2009, 16 (06) : 672 - 676
12345