Unusual strain-dependent thermal conductivity modulation of silver nanoflower-polyurethane fibers

Thermal management of stretchable and wearable electronic devices is an important issue in enhancing performance, reliability, and human thermal comfort. Here, we constructed a unique experimental setup which investigated the strain-dependent thermal conductivity. The thermal conductivity of flower-shaped silver nanoparticle (silver nanoflower)-polyurethane (Ag-PU) composite fibers was systematically investigated as a function of strain. The strain-dependent temperature distribution of the Joule-heated fiber was measured using an infrared camera, and the thermal conductivity was obtained from the 1-dimensional Fourier's conduction model. There was a monotonic decrease in both lattice and electronic thermal conductivity with stretching at 25 degrees C. However, there was an initial increase in lattice and total thermal conductivity in the low strain region (<10%), when the fiber was stretched at 45 degrees C, although the electronic thermal conductivity decreased monotonically. The softening of the polymer at increased temperatures enhanced Poisson's ratio. Resultantly, the fiber cross-sectional area and radial-direction inter-particle distance between silver nanoflowers decreased. This could increase the thermal transport in conductive fibers by modulating the interfaces between silver nanoflowers and polyurethane. A further stretching decreased the lattice thermal conductivity due to the significantly increased axial distance between silver nanoflowers and the decreased filler fraction. The weft-knitted fabric also demonstrated an increased thermal conductance in the low strain region (<= 30%) at 45 degrees C.