The Effect of Acidity Coefficient on the Crystallization Properties and Viscosity of Modified Blast Furnace Slag for Mineral Wool Production

The crystallization and viscosity of modified blast furnace slag are key factors in fiber forming conditions. In this paper, the crystallization behavior of modified blast furnace slag under continuous cooling conditions was studied by differential scanning calorimetry, and its crystallization kinetics with different acidity coefficients were established. On this basis, the evolution law of the crystallization phase and the influence of crystallization on the viscosity of modified blast furnace slag with different acidity coefficients were analyzed. The results indicated that the crystallization phases of slag with acidity coefficients of 1.05 and 1.20 were, respectively, Melilite and Anorthite. During the cooling process at the acidity coefficient of 1.05, the critical rates of precipitation of Melilite and Anorthite were 50 degrees C/s and 20 degrees C/s, respectively, while they were 20 degrees C/s and 15 degrees C/s, respectively, at the acidity coefficient of 1.20. With the increase of the acidity coefficient, the crystal growth mode of slag changed from two-dimensional and three-dimensional mixed crystallization to surface nucleation and one-dimensional crystallization. The crystallization activation energy of slag with acidity coefficients of 1.05 and 1.20 were 698.14 kJ/mol and 1292.50 kJ/mol, respectively. In addition, the change trend of viscosity was related to crystal size and content.