Surface acoustic wave properties of proton-exchanged LiNbO3 waveguides with SiO2 film

Surface acoustic wave (SAW) properties of proton-exchanged (PE) z-cut lithium niobate (LiNbO3) waveguides with silicon dioxide (SiO2) film layers were investigated using octanoic acid. The distribution of hydrogen measured by secondary ion mass spectrometry (SIMS) showed a step-like profile, which was assumed to be equal to the waveguide depth (d). The SiO2 film was deposited on z-cut LiNbO3 waveguide by radio frequency (rf) magnetron sputtering. We investigated the important parameters for the design of SAW devices such as phase velocity (V-p), insertion loss (IL) and temperature coefficient of frequency (TCF) by a network analyzer using thin-film aluminum interdigital transducer electrodes on the upper SiO2 film surface. The experimental results showed that the V-p of SAW decreased slightly with the increase of h/lambda, where h was the thickness of SiO2 films and lambda was the wavelength. The IL of SAW increased with increased h/lambda. The TCF of SAW calculated from the frequency change of the output of SAW delay line showed an evident decrease with the increase of h/lambda. The TCF for PE z-cut LiNbO3 was measured to be about -54.72 ppm/degrees C at h/lambda = 0.08. It revealed that the SiO2 films could compensate and improve the temperature stability as compared with the TCF of SAW on PE samples without SiO2 film.