Superhydrophobic Cerium-Based Coatings on Al-Mg Alloys and Aluminized Steel

被引:3
|
作者
Guerrero-Vaca, Guillermo [1 ]
Rodriguez-Valverde, Miguel A. [2 ]
Castilla-Montilla, Pedro [1 ]
Alguacil-Salamanca, Francisco [1 ]
Rodriguez-Alabanda, Oscar [1 ]
Romero, Pablo E. [1 ]
Molero-Romero, Esther [1 ]
Montes Ruiz-Cabello, F. Javier [2 ]
机构
[1] Univ Cordoba, Dept Mech Engn, Medina Azahara Ave, Cordoba 514071, Spain
[2] Univ Granada, Fac Sci, Appl Phys Dept, LSIP, Campus Fuentenueva S-N, ES-18071 Granada, Spain
关键词
aluminized steel; aluminium-magnesium alloy; superhydrophobic surfaces; sandblasting; cerium coating; electrodeposition; immersion; ELECTRODEPOSITION PROCESS; COTTON FABRICS; SURFACES; SUBSTRATE; FILM;
D O I
10.3390/coatings9120774
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Aluminum-magnesium (Al-Mg) alloy and aluminum-coated steel (aluminized steel) are typically used for the manufacturing of baking trays and molds. For these applications, these materials must be modified to develop release and hydrophobic properties. With this aim, the bare substrates are typically coated with low-surface energy materials such as fluoropolymers, elastomers, or sol-gel layers. In this work, some alternative strategies to prepare these functional surfaces are presented. We used three-step processes involving (i) micro-texturing, (ii) nano layer deposition through immersion and electrodeposition, and (iii) hydrophobization. The raw substrates were sanded or sandblasted at the micro scale, accordingly. Texturization at the nano scale was achieved with a cerium layer formed by electrodeposition or solution immersion. The cerium layers were hydrophobized with fatty acids. The wetting properties of the samples were studied with tilting-plate and bouncing drop methods. We measured the surface roughness of the samples by contact profiling and analyzed their surface morphology using a field emission scanning electron microscope (FESEM). The elemental chemical composition of the samples was analyzed by energy-dispersive X-ray spectroscopy (EDX). The wettability results indicated that the best performance for the Al-Mg substrates was reached by sandblasting and later immersion in a cerium nitrate solution. For aluminized steel substrates, the best results were obtained with both electrodeposition and immersion methods using a cerium chloride solution.
引用
收藏
页数:13
相关论文
共 50 条
  • [1] THE INFLUENCE OF GALVANIC CURRENT ON CERIUM-BASED CONVERSION COATINGS ON MG, AL, AND GALVANIZED STEEL COUPLES
    Maddela, Surender
    O'Keefe, Matthew J.
    Wang, Yar-Ming
    MAGNESIUM TECHNOLOGY 2012, 2012, : 235 - 239
  • [2] Cerium-based conversion coatings on aluminium alloys: a process review
    Harvey, T. G.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2013, 48 (04) : 248 - 269
  • [3] Cerium-based oxide coatings
    Castano, Carlos E.
    O'Keefe, Matthew J.
    Fahrenholtz, William G.
    CURRENT OPINION IN SOLID STATE & MATERIALS SCIENCE, 2015, 19 (02): : 69 - 76
  • [4] Corrosion Properties of Oxide Ceramic Coatings Based on Alloys of the Al-Cu-Mg and Al-Mg Systems
    Bilyi, L. M.
    Posuvailo, V. M.
    Ivashkiv, V. R.
    Kovalchuk, I., V
    MATERIALS SCIENCE, 2021, 57 (02) : 256 - 263
  • [5] Characterization of cerium-based conversion coatings for corrosion protection of aluminum alloys
    Fahrenholtz, WG
    O'Keefe, MJ
    Zhou, HF
    Grant, JT
    SURFACE & COATINGS TECHNOLOGY, 2002, 155 (2-3): : 208 - 213
  • [6] Microstructural evolution of cerium-based coatings on AZ31 magnesium alloys
    Castano, Carlos E.
    O'Keefe, Matthew J.
    Fahrenholtz, William G.
    SURFACE & COATINGS TECHNOLOGY, 2014, 246 : 77 - 84
  • [7] Microelectrochemical Testing of Cerium-Based Conversion Coatings
    Joshi, S.
    Fahrenholtz, W. G.
    O'Keefe, M.
    COATINGS FOR CORROSION PROTECTION, 2010, 25 (29): : 19 - 30
  • [8] ON OXIDATION AND REMOVAL BY DIFFUSION OF MG IN AL AND AL-MG ALLOYS
    FORSVOLL, K
    FOSS, D
    PHILOSOPHICAL MAGAZINE, 1967, 15 (134): : 329 - &
  • [9] Cerium-based conversion layers on aluminum alloys
    Dabalà, M
    Armelao, L
    Buchberger, A
    Calliari, I
    APPLIED SURFACE SCIENCE, 2001, 172 (3-4) : 312 - 322
  • [10] ROLLING TEXTURE OF AL-MG ALLOYS
    KOHARA, S
    INAGAKI, H
    TEXTURES AND MICROSTRUCTURES, 1991, 14 : 1209 - 1214