Structural, morphological and electrical studies of BaCe0.8Y0.2O3-δ synthesized by solution combustion method

被引：9
|
作者：
Jadhav, S. T. [1 ]
Dubal, S. U. [1 ]
Jamale, A. P. [1 ]
Patil, S. P. [1 ]
Bhosale, C. H. [1 ]
Puri, V. R. [1 ]
Jadhav, L. D. [2 ]
机构：
[1] Shivaji Univ, Dept Phys, Kolhapur 416004, Maharashtra, India
[2] Rajaram Coll, Dept Phys, Kolhapur 416004, Maharashtra, India
来源：
IONICS | 2015年 / 21卷 / 05期
关键词：
Chemical synthesis; Oxides; Sintering; Thermogravimetric analysis; Crystal structure; Electrical properties; PROTON; BACEO3; YTTRIUM;
D O I：
10.1007/s11581-014-1304-z
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The 20 % yttrium doped barium cerate (BCY20) powder has been synthesized by cost effective solution combustion method. The flame temperature measured by pyrometer was 1055 A degrees C, less than the adiabatic temperature due to various losses. The phase formation and evolution was studied with TG-DTA and XRD. The carbonate free orthorhombic BCY20 phase was obtained upon calcination at 900 A degrees C. The microstructure of the powders and sintered pellet was examined through scanning electron microscopy. The vibrational mode at 355 cm, characteristics of CeO6 octahedra, was detected in Raman while the bands corresponding to M-O vibrations were revealed in FT-IR. The dc conductivities of sintered pellet measured in argon and air atmospheres at 600 A degrees C were 1.53 x 10(-3) and 1.41 x 10(-3) S/cm.
引用
收藏
页码：1295 / 1300
页数：6
相关论文
共 50 条
  • [1] Structural, morphological and electrical studies of BaCe0.8Y0.2O3-δ synthesized by solution combustion method
    S. T. Jadhav
    S. U. Dubal
    A. P. Jamale
    S. P. Patil
    C. H. Bhosale
    V. R. Puri
    L. D. Jadhav
    Ionics, 2015, 21 : 1295 - 1300
  • [2] Synthesis and electrical properties of BaCe0.8Y0.2O3-α
    Jia, DX
    Ma, GL
    Shi, H
    ACTA CHIMICA SINICA, 2002, 60 (10) : 1737 - 1741
  • [3] Diffusional creep of BaCe0.8Y0.2O3-α mixed conductors
    Goretta, KC
    Park, ET
    Guan, J
    Balachandran, U
    Dorris, SE
    Routbort, JL
    SOLID STATE IONICS, 1998, 111 (3-4) : 295 - 299
  • [4] Dual-layer BaCe0.8Y0.2O3-δ-Ce0.8Y0.2O2-δ/BaCe0.8Y0.2O3-δ-Ni hollow fiber membranes for H2 separation
    Cheng, Hongda
    Wang, Xiaobin
    Meng, Xiuxia
    Meng, Bo
    Sunarso, Jaka
    Tan, Xiaoyao
    Liu, Lihong
    Liu, Shaomin
    JOURNAL OF MEMBRANE SCIENCE, 2020, 601 (601)
  • [5] Diffusional creep of BaCe0.8Y0.2O3-α mixed conductors
    Argonne Natl Lab, Argonne, United States
    Solid State Ionics, 3-4 (295-299):
  • [6] Electrical properties of proton-conducting BaCe0.8Y0.2O3-δ and the effects of bromine addition
    Trivino-Pelaez, Angel
    Perez-Coll, Domingo
    Mather, Glenn C.
    ACTA MATERIALIA, 2019, 167 : 12 - 22
  • [7] Thin film preparation and hydrogen pumping characteristics of BaCe0.8Y0.2O3-δ
    Lee, TH
    Dorris, SE
    Balachandran, U
    SOLID STATE IONICS, 2005, 176 (15-16) : 1479 - 1484
  • [8] Preparation and hydrogen pumping characteristics of BaCe0.8Y0.2O3-δ thin film
    Lee, TH
    Harder, BJ
    Zuo, C
    Dorris, SE
    Balachandran, U
    SOLID STATE IONICS-2004, 2005, 835 : 103 - 108
  • [9] Influence of synthesis route on morphology and conduction behavior of BaCe0.8Y0.2O3-δ
    Sawant, Pooja
    Varma, S.
    Wani, B. N.
    Bharadwaj, S. R.
    JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2012, 107 (01) : 189 - 195
  • [10] The Role of Metal Catalyst on Water Permeation and Stability of BaCe0.8Y0.2O3-δ
    Al, S.
    Zhang, G.
    JOURNAL OF ELECTROCHEMICAL SCIENCE AND TECHNOLOGY, 2018, 9 (03) : 212 - 219
12345