Research on polycrystalline diamond compact (PDC) with low residual stress prepared using nickel-based additive

Polycrystalline diamond compact (PDC) with low residual stress was synthesized using nickel-based additive (Ni70Mn25Co5) as sintering solvent at high temperature/pressure (HTHP) A systematic study of the residual stress in a polycrystalline diamond (PCD) layer was performed using micro Raman spectroscopy The stress was measured by determining the Raman shift and was approximated as being biaxial to calculate the magnitudes of stress Sintering process parameters such as temperature the diamond size and content of binder additive were all found to affect residual stress levels the sample with low stress measured on the surface of PCD is compressive and has an average value of 010 GPa Scanning electron microscopy (SEM) analysis of morphology shows that the dense microstructures with diamond-diamond (D-D) direct bonding has formed in the PCD layer X-ray diffraction (XRD) performed in the cross section of PCD confirmed the presense of diamond nickel-based alloy WC and CoxWxC (C) 2010 Elsevier Ltd All rights reserved